Phosphor, light emitting device and white light emitting diode

A technology of light-emitting devices and phosphors, which is applied in the direction of light-emitting materials, semiconductor devices, electrical components, etc., and can solve problems such as the reduction of luminous intensity

Inactive Publication Date: 2011-03-30
SUMITOMO CHEM CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The phosphors described in these gazettes have lower luminous intensity when the ambient temperature is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphor, light emitting device and white light emitting diode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0081] Lithium carbonate (manufactured by Kanto Chemical Co., Ltd., purity 99%), strontium carbonate (Sakai Chemical Industry Co., Ltd. Manufactured, purity 99% or more), calcium carbonate (manufactured by Ube Materials Co., Ltd., purity 99.9%), europium oxide (manufactured by Shin-Etsu Chemical Co., Ltd., purity 99.99%), silicon dioxide (manufactured by Nippon Aerosil Co., Ltd., purity 99.99%) ), a total of 10 parts by weight of these materials and 150 parts by weight of isopropanol were added in the wet ball mill, and mixed for 4 hours to obtain a slurry. After drying the slurry with an evaporator at 70°C, the resulting metal compound mixture was fired at 900°C for 12 hours in the air, and then slowly cooled (cooling rate 5°C / min) to room temperature (25°C). . Next, after crushing with an agate mortar, the 2 N 2 Firing was carried out at 900° C. for 12 hours in an atmosphere, and then slowly cooled to room temperature (cooling rate: 5° C. / minute), whereby phosphor 2 was o...

Embodiment 2

[0083] Lithium carbonate (manufactured by Kanto Chemical Co., Ltd., purity 99%), strontium carbonate (Sakai Chemical Industry Co., Ltd. Manufactured, purity 99% or more), barium carbonate (Nippon Chemical Industry Co., Ltd., purity 99% or more), europium oxide (manufactured by Shin-Etsu Chemical Co., Ltd., purity 99.99%), silicon dioxide (manufactured by Nippon Aerosil Co., Ltd., purity 99.99%) %) as a raw material, the same operation as in Example 1 was performed to obtain phosphor 3 . Table 1 shows the composition of the phosphor 3, and Table 2 shows the measurement results of the emission intensity.

Embodiment 3

[0085] Lithium carbonate (manufactured by Kanto Chemical Co., Ltd., purity 99%), strontium carbonate (Sakai Chemical Industry Co., Ltd., purity 99% or more), calcium carbonate (Ube Material Co., Ltd., purity 99.9%), europium oxide (Shin-Etsu Chemical Co., Ltd., purity 99.99%), silicon dioxide (Nippon Aerosil Co., Ltd. , purity 99.99%), ammonium chloride (manufactured by Wako Pure Chemical Industries, Ltd., purity 99%), a total of 10 parts by weight of these compounds and 150 parts by weight of isopropanol were added to a wet ball mill and mixed for 4 hours to obtain The slurry. After drying the slurry at 70° C. with an evaporator, the obtained metal compound mixture was fired at 900° C. for 12 hours in an air atmosphere, and then gradually cooled to room temperature. Next, after crushing with an agate mortar, the 2 N 2 After baking at 900° C. for 12 hours in an atmosphere, the phosphor was gradually cooled to room temperature, and Phosphor 4 was obtained. Table 1 shows the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a phosphor, a light emitting device and a white light emitting diode. The phosphor comprises a compound represented by the formula (1) and Eu as an activating agent. Formula: (1) aM12O.bM2O.cM3O2, wherein, M1 is at least one selected from the group consisting of Li, Na, K, Rb and Cs, M2 is at least one selected from the group consisting of Ca, Sr, Ba, Mg and Zn, M3 is at least one selected from the group consisting of Si and Ge, 0.1<=a<=1.5, 0.8<=b<=1.2, 0.8<=a<=1.2, and when M1 is Li, M3 is Si, and a=b=c=1, then M2 is not Sr alone.

Description

technical field [0001] The invention relates to a phosphor, a light emitting device and a light emitting diode. Specifically, the present invention relates to a phosphor having low temperature dependence of emission intensity and excellent thermal stability, a light-emitting device and a light-emitting diode including the phosphor. Background technique [0002] Phosphors are used in light-emitting devices (such as white light-emitting diodes, hereinafter referred to as "LEDs") that use light in the ultraviolet to blue region as an excitation source. As phosphors for white LEDs, for example, the formula Y 3 al 5 o 12 : the compound represented by Ce (Japanese Unexamined Publication No. 10-242513); by (Ba 1-x-y-z Sr x Ca y ) 2 SiO 4 :Eu z The compound represented by the formula Li 2 SrSiO 4 : A compound represented by Eu (International Publication No. 03 / 80763 International Gazette). [0003] The phosphors described in these publications have lower luminous intensi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/59C09K11/61C09K11/66H01L33/00H01L33/32H01L33/50
Inventor 今成裕一郎宫崎进户田健司
Owner SUMITOMO CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com