Method for preparing chemical aluminum oxide by using andalusite as raw material

A technology of andalusite and chemicals, applied in the field of extraction, can solve the problem of unusable tailings, etc., and achieve the effect of low cost, good effect and simplified process

Inactive Publication Date: 2010-08-25
蹬口县欧凯红柱石矿业有限公司 +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of this invention is to propose a method for producing chemical alumina by using tailings after andalusite beneficiation as raw material, which solves the problem that a large amount of tailings cannot be used after andalusite beneficiation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing chemical aluminum oxide by using andalusite as raw material
  • Method for preparing chemical aluminum oxide by using andalusite as raw material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The grade of alumina contained in the andalusite tailings is 45wt%, containing 46wt% of silicon oxide, 2wt% of ferric oxide, and the balance is other impurities.

[0046] The first step: crushing andalusite tailings into balls

[0047] After uniformly mixing 45 parts by weight of andalusite ore with a particle size less than 0.5 mm and 55 parts by weight of an activator with a particle size less than 0.5 mm, pellets with a particle size of 10 mm are obtained through a pelletizing machine;

[0048] Described activator is added the calcium fluoride CaF of 5 weight parts by the calcium oxide CaO of 100 weight parts 2 composition;

[0049] The second step: roasting andalusite self-grinding material

[0050] Roast the pellets prepared in the first step at a temperature of 1300°C for 60 minutes to obtain a calcined material;

[0051] Then the calcined material is moved out of the roasting furnace along with the crucible, and when the temperature of the calcined material in...

Embodiment 2

[0073] The grade of alumina contained in the andalusite tailings is 35wt%, containing 50wt% of silicon oxide, 8wt% of ferric oxide, and the balance is other impurities.

[0074] The first step: crushing andalusite tailings into balls

[0075] After uniformly mixing 50 parts by weight of andalusite ore with a particle size less than 0.5 mm and 50 parts by weight of an activator with a particle size less than 0.5 mm, pellets with a particle size of 60 mm are obtained through a pelletizing machine;

[0076] Described activator is added the calcium fluoride CaF of 1 weight part by the calcium oxide CaO of 100 weight parts 2 composition;

[0077] The second step: roasting andalusite self-grinding material

[0078] Roast the pellets prepared in the first step at a temperature of 1100°C for 90 minutes to obtain a calcined material;

[0079] Then the calcined material is moved out of the roasting furnace along with the crucible. When the temperature of the calcined material in the ...

Embodiment 3

[0103] The grade of alumina contained in the andalusite tailings is 52wt%, containing 38wt% of silicon oxide, 4wt% of ferric oxide, and the balance is other impurities.

[0104] The first step: crushing andalusite tailings into balls

[0105] After uniformly mixing 40 parts by weight of andalusite ore with a particle size less than 0.5 mm and 60 parts by weight of an activator with a particle size less than 0.5 mm, pellets with a particle size of 30 mm are obtained through a pelletizing machine;

[0106] Described activator is added the calcium fluoride CaF of 3 weight parts by the calcium oxide CaO of 100 weight parts 2 composition;

[0107] The second step: roasting andalusite self-grinding material

[0108] Roasting the pellets prepared in the first step at a temperature of 1200°C for 90 minutes to obtain a calcined material;

[0109] Then the calcined material is moved out of the roasting furnace along with the crucible. When the temperature of the calcined material in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of alumina chemicals by using andalusite as raw materials. Gangue obtained from ore dressing of the andalusite ore is adopted as raw materials and treated with ball making, baking, multi-stage separation, additive adding and granulation to extract the alumina chemicals with the purity of 99.5 to 99.999 percent, which leads andalusite resource to be comprehensively utilized with resource conservation as well as environmental protection.

Description

technical field [0001] The present invention relates to an extraction method, more particularly, refers to a method for producing chemical alumina by using tailings after beneficiation of andalusite as raw material. Background technique [0002] Chemical alumina is non-metallurgical alumina series, mainly including special ceramic alumina series, activated alumina series, granulated powder series, alumina series for special refractory materials, alumina series for grinding and polishing, etc., widely used in chemical industry, Ceramics, refractory materials and military industries, etc., the consumption is very large, and the market prospect is broad. [0003] At present, the raw material for the world's production of chemical alumina is bauxite. However, if andalusite ore is selected from andalusite concentrate through ore dressing as a raw material for refractory materials, the alumina grade needs to be greater than 57%, and the yield is only 12-15%. Utilization, stackin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F7/30
Inventor 卢惠民苏学民韩国雄
Owner 蹬口县欧凯红柱石矿业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com