Benzoxazine compositions with core shell rubbers

A composition, benzoxazine technology, applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problem of not meeting the needs of heat-curable compositions

Active Publication Date: 2009-11-11
汉高知识产权及控股有限公司
View PDF15 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] Despite these prior art, the market demand for thermally curable compositions based on combinations of benzoxazines and core-shell rubbers prepared from bisphenol A, formaldehyde and alkylamines remains unmet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Benzoxazine compositions with core shell rubbers
  • Benzoxazine compositions with core shell rubbers
  • Benzoxazine compositions with core shell rubbers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0064] Here a series of samples were prepared from benzoxazine and epoxy resin, core shell rubber, nanoparticulate silica and / or epoxidized p-aminophenol as shown in Tables 1a and 1b below. Sample Nos. 1, 4, and 7 are listed as controls without core-shell rubber, relative to Sample Nos. 2-3, 5-6, and 8, respectively.

Table 1a

Table 1b

1 Benzoxazines also include monofunctional benzoxazines.

*Epoxidized p-aminophenol, commercially available from Huntsman Specialty Chemical.

[0065] Prepare each sample as follows:

[0066] Warming the benzoxazine at 160°F made it flowable without initiating cure.

[0067] The remaining ingredients were added to the speedmixer vessel and heated with mixing at a mixing speed of 2400 rpm for a period of 15 minutes at a temperature of 160°F until a substantially homogeneous composition was observed to form. The composition thus formed was poured directly into the mold before curing.

[0068] Thus, in an autoclave, the samples des...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

Curable compositions, such as benzoxazine-based ones together with core shell rubbers, are useful in applications within the aerospace industry, such as for example as heat curable composition for useas a matrix resin or an adhesive, and form the basis of the present invention.

Description

technical field [0001] Curable compositions, such as benzoxazine-based compositions with core-shell rubber, are useful in aerospace industry applications, for example as heat-curable compositions for use as matrix resins or adhesives, and form the basis of the present invention . Background technique [0002] Epoxy resins with various hardeners are widely used in the aerospace and electronics industries as adhesives and as matrix resins for use in prepreg assemblies with various substrates. [0003] It is reported in the literature that benzoxazines themselves generally have a high glass transition temperature, good electrical properties (eg, dielectric constant), and low flammability. [0004] Blends of epoxy resins and benzoxazines are known. See, eg, US Patent Nos. 4,607,091 (Schreiber), 5,021,484 (Schreiber), 5,200,452 (Schreiber), and 5,445,911 (Schreiber). These blends show potential use in the electronics industry, as the epoxy resin reduces the melt viscosity of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08K5/35C08L51/00C08L21/00C09J7/35
CPCC08K5/357C08K3/36C08L63/00C08J2363/00C09J11/06C09J7/35C08L51/04C09J2301/408C08J5/241C08J5/244C08J5/243C08J5/242
Inventor S·L·莱曼W·H·李R·S·翁
Owner 汉高知识产权及控股有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap