A condom and lubricating technology, which is applied in the field of lubricating oil for condoms, can solve the problems of greasy and easy to dry lubricating oil, easily cause sexual pain, unsatisfactory lubricating effect, etc., and achieve the effect of long-lasting lubricating performance and clear and transparent appearance

Active Publication Date: 2012-12-12
SHANGHAI MINGBANG RUBBER PROD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this lubricating oil is greasy and easy to dry, the lubricating effect is not ideal, and it is easy to cause pain during sexual intercourse

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0012] Example 1: The determined target viscosity is n=1000mm 2 / s, the quality of the target lubricating oil is 10kg, that is, X1+X2=10kg, and the viscosity of low-viscosity silicone oil is n2=0.65mm 2 / s, the relationship between the viscosity n1 of high-viscosity silicone oil and the quality X1, X2 is as follows:

[0013] n1

X1

X2

10 million

4.34

5.56

5000000

4.62

5.38

3000000

4.78

5.22

1000000

4.84

5.16

500000

5.4

4.6

100,000

6.14

3.86

10000

7.6

2.4

0.5 million

8.2

1.8

[0014] In the above example, change n2 to 900m m 2 / s, other things remain unchanged, then the relationship between n1 and X1, X2 is as follows:

[0015] n1

example 2

[0016] Example 2, determine the target viscosity n = 500mm 2 / s, the quality of the target lubricating oil is 10kg, that is, X1+X2=10kg, the viscosity of low-viscosity silicone oil n2=0.65mm 2 / s, the relationship between the viscosity n1 of high-viscosity silicone oil and the quality X1, X2 is as follows:

[0017] n1

X1

X2

10 million

4.01

5.99

5000000

4.19

5.81

3000000

4.33

5.67

1000000

4.66

5.34

500000

4.9

5.1

100,000

5.58

4.42

10000

6.89

3.11

0.5 million

7.4

2.6

[0018] In this example, use n2=200m m instead 2 / s, and the rest remain unchanged, then the relationship between n1 and X1, X2 is as follows:

[0019] n1

example 3

[0020] Example 3: Determine the target viscosity n=200mm 2 / s. The target lubricating oil quality is 10kg, that is, X1+X2=10kg, and the viscosity of low-viscosity silicone oil n2=0.65, then the relationship between n1 and X1, X2 is as follows:

[0021] n1

X1

X2

10 million

3.4

6.6

5000000

3.6

6.4

3000000

3.7

6.3

1000000

4

6

500000

4.22

5.78

100,000

4.7

5.3

10000

6

4

0.5 million

6.4

3.6

[0022] In this example, use n2=100m m instead 2 / s, then the relationship between n1 and X1, X2 is as follows:

[0023] n1

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of contraceptives, particularly relates to high-lubricity compound silicone oil for a condom. The compound silicone oil is formed by high-viscosity silicone oil and low-viscosity silicone oil by a certain weight ratio in a complex formulation way, the compound silicone oil, the high-viscosity silicone oil and the low-viscosity silicone oil satisfy the following basic relation formula: (X1+X2)lgn=X1lgn1+X2lgn2, wherein n1, n2 and n3 are respectively the viscosity of the three silicone oils, and (X1+X2), X1 and X2 are respectively the quality of the three silicone oils. Compared with silicone oil with single viscosity, the compound silicone oil greatly improves the lubricity, and can be durable without drying. The condom using the compound silicone oil is suitable for contraception of numerous women, and is particular suitable for young females to use when being in a growth period and a lactation period to generate colpoxerosis because of emotional tension and violent exercise.

Description

technical field [0001] The invention belongs to the technical field of contraceptive products, and in particular relates to a lubricating oil for a condom. Background technique [0002] At present, most of the lubricating oils used in condoms (also known as condoms) are simethicone (abbreviated as silicone oil, the same below). Its viscosity is generally in the range of 5 to 1000mm 2 / s range, and all use simethicone oil with a single viscosity. This lube is applied to the outside of the rubber condom and acts to lubricate the vagina during intercourse. However, this lubricating oil is greasy and easy to dry, the lubricating effect is not ideal, and it is easy to cause pain during sexual intercourse. Contents of the invention [0003] The object of the present invention is to provide a condom lubricating oil with good lubricating effect. [0004] After research, it is found that a compound silicone oil with suitable viscosity can be obtained after a certain amount of h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L31/12
Inventor 蔡启杰
Owner SHANGHAI MINGBANG RUBBER PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap