Production technology of arge-particle ceramic tile

A production process and large particle technology, applied in clay processing equipment, clay preparation devices, chemical instruments and methods, etc., can solve the problems of environmental damage, waste of clay resources, etc., and achieve the effect of reducing the amount of use

Inactive Publication Date: 2011-06-22
黄家洞
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the other hand, the waste bricks with clay as the main material are discarded because they cannot continue to be used as building materials, which not only causes damage to the environment, but also wastes limited clay resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production technology of arge-particle ceramic tile
  • Production technology of arge-particle ceramic tile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be described in detail below in conjunction with accompanying drawing and specific embodiment:

[0019] A specific embodiment of the present invention, such as figure 1 Shown, a kind of large particle ceramic tile production process, the specific steps of this process are:

[0020] Step 1: Batching, which is to mix the raw materials required for the production of ceramics in proportion, and then add them to the ball mill. The specific process is to use a forklift to pour raw materials such as clay and ore into the weighing device of the feeding system according to the weight ratio of the ingredients, and then add them to the ball mill through the feeding system;

[0021] Step 2: Ball milling, that is, the raw materials and water prepared according to the ratio are sent to the ball mill together. During the rolling process of the ball mill, the raw materials and water are broken under the action of ball stones, so that the shape and size of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention mainly aims to provide a production technology of an energy-saving, environmentally-friendly and attractive large-particle ceramic tile aiming at the deficiency in the prior art, thereby realizing the purposes of fully utilizing clay resources and reusing waste bricks. The production technology mainly comprises the following working procedures: burdening, ball milling, pulping, screening to remove iron, spraying, drying, aging and the like to obtain a main toner material; evenly stirring the broken and screened large-particle brick points by a mixing mechanism into the main toner material to serve as the powder of the large-particle ceramic tile; putting the above powder into a press die to press and shape; putting a dried best green body into a roller kiln; and baking the dried best green body at high temperature.

Description

technical field [0001] The invention relates to the technical field of production and manufacture of building ceramic bricks, in particular to an environment-friendly production process of large-grain ceramic bricks. Background technique [0002] Ceramic tiles are products often used in construction and home furnishing. They are mainly made of clay. However, excessive excavation of clay will cause certain damage to the environment, and even cause large areas of farmland to be unusable. Therefore, it is very important to make full use of the precious non-renewable limited clay resources. On the other hand, the waste bricks with clay as the main material are discarded because they cannot continue to be used as building materials, which not only causes damage to the environment, but also wastes limited clay resources. [0003] The present invention aims at the above problems and proposes a good technical solution to achieve full utilization of clay resources and reuse of waste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine