Pumice straw lightweight aggregate concrete and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A lightweight aggregate concrete and straw technology, which is applied in ceramic products, other household utensils, sustainable waste treatment, etc., can solve the problems of poor workability between light raw materials and concrete, high density of lightweight aggregate concrete, and poor thermal insulation effect Good and other problems, to achieve the effect of light weight, reduced cement consumption, good toughness
Inactive Publication Date: 2012-10-31
HEBEI INSTITUTE OF ARCHITECTURE AND CIVIL ENGINEERING
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The present invention provides a kind of pumice straw lightweight aggregate concrete and its preparation method, to solve the problems of high raw material cost and high production energy consumption of existing lightweight aggregate concrete; and to solve the problem of poor workability between light raw materials and concrete, resulting in a large amount of cement slurry It is sucked into the hole during mixing, the density of lightweight aggregate concrete is high, the thermal conductivity is high, and the technical problem of thermal insulation effect is not good; it also solves the technical problems that the preparation method of ordinary lightweight aggregate concrete is easy to delaminate inside the concrete when mixing, which affects Technical issues with product performance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0041] Embodiment 1, this kind of pumice straw light aggregate concrete, its raw material ratio by weight is as follows:
[0042] 1 part of cement;
[0043] 0.43 parts of fly ash;
[0044] 2.3 parts of pumice sand;
[0045] Corn straw fiber 0.04 parts;
[0046] Admixture 0.015 parts;
[0047] Foaming agent 0.006 part;
[0048] 0.53 parts of water.
Embodiment 2
[0049] Embodiment two, this kind of pumice straw light aggregate concrete, its raw material proportioning by weight is as follows:
[0050] 1 part of cement;
[0051] 0.42 parts of fly ash;
[0052] 2.55 parts of pumice sand;
[0053] Corn straw fiber 0.05 parts;
[0054] Admixture 0.012 parts;
[0055] Foaming agent 0.007 part;
[0056] 0.55 parts of water.
Embodiment 3
[0057] Embodiment three, this kind of pumice straw light aggregate concrete, its raw material proportioning by weight is as follows:
[0058] 1 part of cement;
[0059] 0.50 parts of fly ash;
[0060] 2.05 parts of pumice sand;
[0061] Corn straw fiber 0.05 part;
[0062] Admixture 0.010 parts;
[0063] Foaming agent 0.005 part;
[0064] 0.55 parts of water.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
length
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
Login to View More
Abstract
Pumice straw lightweight aggregate concrete and a preparation method thereof. The raw materials of the pumice straw lightweight aggregate concrete comprise, by weight, 1 part of cement, 0.40-0.50 part of fly ash, 2.05-2.55 parts of pumice sand, 0.03-0.05 part of corn straw fibers, 0.010-0.015 part of an additive, 0.005-0.007 part of a foaming agent, and 0.50-0.55 part of water. The preparation method provided by the invention comprises: Step 1, preparing thin shell pumice sand and thin shell straw fibers; Step 2, pouring the cement, fly ash, water and additive according to the ratio as well as the prepared thin shell pumice sand into a mixer with uniformly stirring; Step 3, pouring the thin shell straw fibers into the mixer with further stirring; Step 4, whisking the foaming agent, pouring the foaming agent into the above stirred substances, followed by stirring to produce the pumice straw lightweight aggregate concrete. According to the invention, the mechanical properties of the lightweight aggregate concrete are effectively raised, the heat insulation performance is enhanced, and the production cost is reduced.
Description
technical field [0001] The invention relates to a lightweight aggregate concrete and a preparation method thereof. Background technique [0002] Light aggregate concrete is light concrete made of light aggregate with a bulk density not greater than 1900 kg / m, also known as porous aggregate light concrete. Because light aggregate concrete contains a large number of closed pores, it has light weight, good thermal insulation performance, and convenient construction. Compared with ordinary concrete of the same grade, it can reduce its own weight by more than 20-30%. Existing lightweight aggregate concrete is usually prepared into foam by mechanical means, and then the foam is added to the slurry composed of siliceous materials, calcium materials, water and various admixtures, etc. After mixing, stirring, It is formed by pouring and curing. At present, ceramsite, slag, pumice, expanded perlite, polystyrene foam plastic particles, etc. are mainly used as light raw materials. Th...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.