Polyvinyl chloride-polyvinylidene emulsion based concrete bridge structure surface protective coating material and preparation method thereof

A chlorine partial emulsion and bridge structure technology, which is applied in coatings and other directions, can solve problems such as poor anti-aging performance, high coating dosage, and loss of protective effect of coatings, and achieve excellent anti-aging performance, simple painting process, and excellent protection effect of effect

Inactive Publication Date: 2015-04-08
CCCC CIVIL ENG SCI & TECH +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the existing concrete surface protective coatings mainly have the following shortcomings: First, the anti-carbonation performance is poor, and the carbonation depth is generally greater than the specification requirements (standard requirements ≤ 1mm), concrete The phenomenon of carbonization corrosion is serious, which in turn causes the corrosion of internal steel bars, leading to concrete rust and peeling and other diseases; second, the anti-aging performance is poor, and similar domestic protective coatings will appear wrinkling, yellowing, cracking, powdering, etc. to varying degrees in about 800 hours The aging damage of the paint causes the paint to lose its protective effect; the third is that the painting process is complicated and the coating dosage is large. Before painting, domestic similar products often need to apply a layer of primer on the concrete surface, and then paint 2~3 coats For protective coatings, the coating dosage is about 0.5Kg / m2~1.0Kg / m2; the fourth is poor environmental protection, and many of the existing domestic concrete protective coatings contain VOC , causing harm to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyvinyl chloride-polyvinylidene emulsion based concrete bridge structure surface protective coating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] The concrete bridge structure surface protective coating material based on chlorine partial emulsion is made of the following substances by weight:

[0067] 80 parts of chlorine partial emulsion;

[0068] 1 part bentonite;

[0069] 0.3 parts of water-based anti-aging agent;

[0070] 1 part of titanium dioxide;

[0071] 1 part sericite;

[0072] 2 parts of functional auxiliary system;

[0073] 2 parts of adjusting auxiliary system.

[0074] Wherein, the chlorine partial emulsion solid content is 40%;

[0075] Water-based anti-aging agent chooses water-based anti-aging agent SL-02;

[0076] Titanium dioxide choose titanium dioxide RX-237;

[0077] Sericite selects sericite GA-1;

[0078] The functional additive system is composed of hydrophobic agent, stain-resistant agent, and adhesion promoter mixed in a mass ratio of 10:2:3; among them, the hydrophobic agent is selected from the hydrophobic agent lotus leaf biphobic SS-02, and the stain-resistant agent is selec...

Embodiment 2

[0087] The concrete bridge structure surface protective coating material based on chlorine partial emulsion is made of the following substances by weight:

[0088] 85 parts of chlorine partial emulsion;

[0089] 2 parts of bentonite;

[0090] 0.6 parts of water-based anti-aging agent;

[0091] 3 parts of titanium dioxide;

[0092] Sericite 3 parts;

[0093] 6 parts of functional auxiliary system;

[0094] Adjust 5 parts of auxiliary system.

[0095] Wherein, the chlorine partial emulsion solid content is 40%;

[0096] Water-based anti-aging agent chooses water-based anti-aging agent SL-02;

[0097] Titanium dioxide choose titanium dioxide RX-237;

[0098] Sericite selects sericite GA-1;

[0099] The functional additive system is composed of hydrophobic agent, stain-resistant agent, and adhesion promoter mixed in a mass ratio of 10:2:3; among them, the hydrophobic agent is selected from the hydrophobic agent lotus leaf biphobic SS-02, and the stain-resistant agent is se...

Embodiment 3

[0108] The concrete bridge structure surface protective coating material based on chlorine partial emulsion is made of the following substances by weight:

[0109] 90 parts of chlorine partial emulsion;

[0110] 3 parts of bentonite;

[0111] 1 part of water-based anti-aging agent;

[0112] 5 parts of titanium dioxide;

[0113] Sericite 5 parts;

[0114] 10 parts of functional auxiliary system;

[0115] 9 parts of adjusting auxiliary system.

[0116] Wherein, the chlorine partial emulsion solid content is 40%;

[0117] Water-based anti-aging agent chooses water-based anti-aging agent SL-02;

[0118] Titanium dioxide choose titanium dioxide RX-237;

[0119] Sericite selects sericite GA-1;

[0120] The functional additive system is composed of hydrophobic agent, stain-resistant agent, and adhesion promoter mixed in a mass ratio of 10:2:3; among them, the hydrophobic agent is selected from the hydrophobic agent lotus leaf biphobic SS-02, and the stain-resistant agent is s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a polyvinyl chloride-polyvinylidene emulsion based concrete bridge structure surface protective coating material and a preparation method thereof. Most of existing concrete surface protective coatings are poor in carbonization resistance and ageing resistance and complex in painting process. The coating material is composed of 80-90 parts of polyvinyl chloride-polyvinylidene emulsion, 1-3 parts of bentonite, 0.3-1 part of aqueous antiager, 1-5 parts of titanium dioxide, 1-5 parts of sericite, 2-10 parts of functional assistant system and 2-9 parts of adjustment assistant system, wherein the adjustment assistant system is composed of antifoaming agent, dispersing agent and leveling thickener according to the mass ratio of 2:1:4. The coating material enables concrete to have excellent protective effects under accelerated carbonizing conditions, carbonization of the concrete is decelerated, the coating material is excellent in ageing resistance, the coating painting process is simple, all procedures from production to construction are safe and environment-friendly, and environment pollution is avoided.

Description

technical field [0001] The invention belongs to the technical field of concrete protection, and in particular relates to a protective coating material for the surface of concrete bridge structures based on chlorine partial emulsion and a preparation method thereof. Background technique [0002] Concrete is a widely used building material with excellent durability, but under the long-term erosion of the general atmospheric environment (carbon dioxide, water, oxygen, etc.) and its own performance defects (pores, micro-cracks, etc.), concrete carbonation will occur Corrosion, and directly lead to the occurrence of corrosion of its internal steel bars, thus causing a series of diseases such as concrete spalling, rust swelling cracks, etc., seriously restricting the durability and safety of concrete bridges. [0003] Carbonation of concrete is mainly due to CO 2 Diffusion penetrates into the interior of the concrete, and the pores near the reinforcement in the concrete Ca(OH) ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D127/08C09D7/12C04B41/50
Inventor 丁小军葛胜锦潘长平彭泽友翟敏刚盖卫鹏吕晓霞赵秋华汪明天
Owner CCCC CIVIL ENG SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products