Preparation method of composite projectile wing
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A composite material and elastic wing technology is applied in the preparation of composite material elastic wings and the field of elastic wing preparation. Effect
Active Publication Date: 2016-03-02
湖北三江航天江北机械工程有限公司
View PDF1 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The traditional molding process of the wing adopts the aluminum alloy skeleton + metal skin structure. Therefore, when the strength and stiffness indicators are met, the quality index of the wing is seriously exceeded.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0027] Working conditions and requirements:
[0028] Tensile strength / MPa
≥400
Tensile modulus / GPa
≥20
Bending strength / MPa
≥400
Flexural modulus / GPa
≥20
150℃bending strength / MPa
≥320
Mass / Kg
≤15
Product length / m
2.4
[0029] 1) According to the product quality and external dimensions, through the analysis and calculation of ANSYS finite element software, the best lay-up angle is set to 0°, ±30°, ±45°, ±60°, ±80°, 90°, a total of 11 layers , the ply angle as figure 2 shown.
[0030] 2) Cut 11 pieces of T300 carbon fiber cloth according to 0°, 0°, ±30°, ±45°, ±60°, ±80°, and 90° respectively. According to the product size requirements, the size of the carbon fiber cloth is required to be 2600mm*1000mm.
[0031] 3) Embed two pieces of aluminum metal parts 11 in the polymethacrylimide foam material so as to facilitate the matching and load bearing of the product and the engine, and the two pi...
Embodiment 2
[0038] Working conditions and requirements:
[0039] Tensile strength / MPa
≥350
Tensile modulus / GPa
≥20
Bending strength / MPa
≥350
Flexural modulus / GPa
≥20
Weight / Kg
≤10
Product length / m
2.4
[0040] 1) According to the requirements of product quality and external dimensions, through the analysis and calculation of ANSYS finite element software, set the layup angle to 0°, ±45°, ±80°, ±90°, a total of 8 layers, the layup angle is as follows figure 2 shown.
[0041] 2) Cut 8 pieces of T300 carbon fiber cloth according to 0°, 0°, ±45°, ±80°, and ±90° respectively, and the size of the carbon fiber cloth is 2600mm*1000mm.
[0042] 3) Embed two pieces of aluminum metal parts 11 in the polymethacrylimide foam material, so as to facilitate the assembly and load bearing of the product and the engine, and the two pieces of aluminum metal parts can be the same or different.
[0043] 4) Lay 8 pieces of T300 carbon...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
tensile strength
aaaaa
aaaaa
bending strength
aaaaa
aaaaa
flexural modulus
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses a preparation method of a composite material missile wing. The method comprises the following steps: setting the best laying angle and laying thickness, calculating the quantity of fiber cloth at each angle, cutting the fiber cloth according to the set laying angle and the calculated quantity of the fiber cloth, embedding at least two metal pieces into foam material, gradually laying the cut fiber cloth on upper and lower surfaces of the foam material according to the designed laying angle and sequence so as to obtain a premolded body, installing the premolded body in a rigid forming die, and performing solidification forming through a resin transfer molding technology, so as to obtain the composite material missile wing. The missile wing prepared by the method has the characteristics of low weight, high rigidity, uniform apparent color and good uniformity of external dimensions.
Description
technical field [0001] The invention belongs to the technical field of weapon preparation, and in particular relates to a method for preparing a wing, in particular to a method for preparing a wing made of composite materials. Background technique [0002] The wings installed under the tail of the UAV booster have a large-scale structural feature, and its function is to increase the stability of the UAV and provide a certain lift. The traditional forming process of the wing adopts aluminum alloy skeleton + metal skin structure. Therefore, when the strength and stiffness indicators are met, the quality index of the wing is seriously exceeded. [0003] Polymethacrylimide foam material was first successfully developed in Germany and started industrial production. It has the characteristics of low density, high temperature resistance, compression resistance and high specific strength, and has excellent secondary processing performance. Processing and molding, it has good compre...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More