A kind of anti-ultraviolet bamboo charcoal viscose fiber and preparation method thereof

A viscose fiber and bamboo charcoal viscose technology, applied in the field of ultraviolet-resistant bamboo charcoal viscose fiber and its preparation, can solve problems such as poor spinnability of bamboo charcoal viscose fiber, and achieve remarkable deodorizing function, good air permeability, and comprehensive ultraviolet resistance. Effect

Active Publication Date: 2015-09-16
YIBIN HIEST FIBER +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention is aimed at above-mentioned technical problem, simultaneously in order to adapt to the demand of product market customer, solves the problem of poor spinnability of bamboo charcoal viscose fiber, provides a kind of anti-ultraviolet bamboo charcoal viscose fiber and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] An anti-ultraviolet bamboo charcoal viscose fiber. The anti-ultraviolet bamboo charcoal solution is mixed with viscose by injection before spinning, and the finished product is obtained through wet spinning and post-treatment. The anti-ultraviolet bamboo charcoal solution is mixed with anti-ultraviolet masterbatch and bamboo charcoal solution Made; the anti-ultraviolet masterbatch contains anti-ultraviolet agent, by weight, the content of anti-ultraviolet agent in the fiber is 0.2%, the content of bamboo charcoal is 0.5%, the ultraviolet shielding rate is ≥ 95%, the ammonia absorption rate is ≥ 50%, and the air permeability is ≥ 500mm / s, color fastness to washing level 4.

Embodiment 2

[0046] A kind of anti-ultraviolet bamboo charcoal viscose viscose filament, the anti-ultraviolet bamboo charcoal solution is mixed with viscose by pre-spinning injection, and the finished product is obtained through wet spinning and post-treatment. The anti-ultraviolet bamboo charcoal solution is composed of anti-ultraviolet masterbatch and Bamboo charcoal solution is mixed; anti-ultraviolet masterbatch contains anti-ultraviolet agent, by weight, anti-ultraviolet agent content in fiber is 0.01%, bamboo charcoal content is 0.1%, ultraviolet shielding rate is ≥ 95%, ammonia absorption rate is ≥ 50%, air permeability ≥500mm / s, color fastness to washing 4 grades, dry strength 1.6cN / dtex, dry elongation 18%, dry elongation variation ≤ 8%.

Embodiment 3

[0048] A kind of anti-ultraviolet bamboo charcoal viscose viscose filament, the anti-ultraviolet bamboo charcoal solution is mixed with viscose by pre-spinning injection, and the finished product is obtained through wet spinning and post-treatment. The anti-ultraviolet bamboo charcoal solution is composed of anti-ultraviolet masterbatch and Bamboo charcoal solution is mixed; anti-ultraviolet masterbatch contains anti-ultraviolet agent, by weight, anti-ultraviolet agent content in fiber is 2%, bamboo charcoal content is 5%, ultraviolet shielding rate ≥ 95%, ammonia absorption rate ≥ 50%, air permeability ≥500mm / s, color fastness to washing is grade 5, dry strength 2.0cN / dtex, dry elongation 19%, dry elongation variation ≤8%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

In order to meet the needs of customers in the product market and solve the problem of poor spinnability of the bamboo charcoal viscose fiber, the invention provides a UV-resistant bamboo charcoal viscose fiber and a preparation method thereof. It is characterized in that: the anti-ultraviolet bamboo charcoal solution is mixed with viscose by injection before spinning, and the finished product is obtained through wet spinning and post-treatment. The anti-ultraviolet bamboo charcoal solution is formed by mixing anti-ultraviolet masterbatch and bamboo charcoal solution; The masterbatch contains anti-ultraviolet agent, by weight, the content of anti-ultraviolet agent in the fiber is 0.01~10%, the content of bamboo charcoal is 0.1~10%, the ultraviolet shielding rate is ≥95%, the ammonia absorption rate is ≥50%, and the air permeability is ≥500mm / s , Color fastness to washing 4~5 grades. The anti-ultraviolet bamboo charcoal viscose fiber of the present invention not only has anti-ultraviolet and deodorizing functions, but also has good air permeability and hygroscopicity, and the anti-ultraviolet effect is stronger than that of ordinary bamboo charcoal fibers, the breaking strength of the fibers is high, and the cost is low.

Description

technical field [0001] The invention relates to the technical field of viscose in the textile industry, in particular to an anti-ultraviolet bamboo charcoal viscose fiber and a preparation method thereof. Background technique [0002] Bamboo charcoal is mainly composed of carbon, hydrogen, oxygen and other elements. It is hard, fine and porous, and has strong adsorption capacity. Excellent deodorizing, antiseptic, and odor-absorbing functions. Nano-scale bamboo charcoal powder also has good antibacterial and bactericidal effects, can absorb and neutralize the acidic substances contained in sweat, and achieve the effect of whitening the skin. Not only that, bamboo charcoal is also a very good emission material for far infrared and negative ions. Bamboo-charcoal blended health-care fiber can emit negative ions without damaging equipment during processing, which overcomes the serious disadvantage of grinding needles when processing fabrics with negative ion fibers, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F2/08D01D13/00D01D5/06
Inventor 冯涛邓传东李蓉玲毛远航陈晓芳
Owner YIBIN HIEST FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com