A kind of strong penetration waterproofing agent and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A water repellent, strong technology, applied in the direction of coating, can solve the problems of poor water resistance, complex preparation method, poor permeability, etc., to achieve the effect of strong temperature resistance, broad application prospects and simple production method
Active Publication Date: 2017-05-24
WUHAN PANTHERS LEAKPROOF TECH DEV CO LTD
View PDF6 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0008] (3) The Si-O bond length is longer, and the Si-O-Si bond angle is large
[0047] So far, all kinds of waterproofing agents have been sold in the market, but they all have their defects: high temperature resistance, slow drying, poor permeability, change of original color, poor water resistance, complicated preparation methods, and cannot meet the needs of the market
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0070] 1. The ratio of strong penetrating waterproofing agent for the inner and outer walls of the building (mass ratio)
[0071]
[0072] 2. Preparation method
[0073] (1) Take 2.0 kg of organic silicon polymer, add 97.6 kg of co-solvent under stirring, and react at 30°C for 1 hour;
[0074] (2) When the reactant is translucent, add 0.11 kg of penetrant under stirring, and react at 30°C for 0.5 hours;
[0075] (3) When the reactant is translucent, add 0.11kg of leveling agent under stirring, and react at 30°C for 0.5 hours;
[0076] (4) When the reactant is translucent, add 0.11 kg of defoamer under stirring, and react at 30°C for 0.5 hours;
[0077] (5) When the reactant is translucent, add 0.11 kg of dispersant under stirring, and react at 30°C for 0.5 hours;
[0078] (6) Filtered by 300 mesh stainless steel mesh, packaged and stored.
Embodiment 2
[0080] 1. The ratio of strong penetrating waterproofing agent for ancient buildings (mass ratio)
[0081]
[0082]
[0083] 2. Preparation method
[0084] (1) Take 1.9kg of organosilicon polymer, add 97.5kg of cosolvent under stirring, and react at 25℃ for 1 hour; (2) When the reactant is transparent, add 0.2kg of penetrant under stirring, and react at 25℃ for 0.5 hour ;
[0085] (3) When the reactant is translucent, add 0.2kg of leveling agent under stirring, and react at 25°C for 0.5 hours;
[0086] (4) When the reactant is translucent, add 0.15 kg of defoamer under stirring, and react at 25°C for 0.5 hours;
[0087] (5) When the reactant is translucent, add 0.15 kg of dispersant while stirring, and react at 25°C for 0.5 hours;
[0088] (6) Filtered by 300 mesh stainless steel mesh, packaged and stored.
[0089] Test report of the strong penetrating waterproofing agent prepared according to Example 1 (see attachment).
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a strong permeability waterproof agent and a preparation method thereof. The strong permeability waterproof agent comprises the following raw materials by following mass fraction: 1.8-2.5 parts of organosilicon polymer, 0.1-0.3 parts of osmotic agent, 0.1-0.3 parts of levelling agent, 0.1-0.3 parts of antifoaming agent, 0.1-0.3 parts of dispersing agent and 96-98 parts of cosolvent. The waterproof agent is prepared by adding the ingredients in a container one by one and then stirring, controlling the temperature and filtering under normal pressure condition. The strong permeability waterproof agent has the advantages of production technology simplification, prevention of high temperature / high pressure synthesis risk, and no three wastes generation of composition; and has the beneficial effects of strong high-temperature resistance, strong permeability, fast drying and no change of color of original product. The strong permeability waterproof agent can be widely used for moisture and mildew resistant treatment before interior decoration, and used for water repellent treatment in stone industry, woodwork and textile industry, and is especially suitable for rapid construction under special environment.
Description
Technical field [0001] The invention relates to a waterproofing agent, in particular to a strong penetrating waterproofing agent and a preparation method thereof. Background technique [0002] 1 Silicone [0003] Organosilicon, or organosilicon compound, refers to a compound that contains Si-O bonds and at least one organic group is directly connected to the silicon atom. It is customary to use oxygen, sulfur, nitrogen, etc. to connect the organic group to the silicon atom. The connected compounds are also regarded as organosilicon compounds. Among them, the polysiloxane composed of silicon-oxygen bond (-Si-0-Si-) is the largest, most researched and most widely used type of organosilicon compounds, accounting for more than 90% of the total amount. . [0004] The basic structural unit of organic silicon products is composed of silicon-oxygen chain links, and the side chains are connected to various other organic groups through silicon atoms. Therefore, the structure of organic sil...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 