Solidifying agent of epoxy resin for reinforcing and sealing, and method of preparing the same

A technology for epoxy resin curing and sealing, applied in the field of epoxy resin curing agent, can solve problems such as poor activity, affect construction, and difficult to cure, and achieve the effects of avoiding the risk of high temperature and high pressure synthesis, simple production method, and mild curing

Inactive Publication Date: 2011-04-13
湖北湖大资产经营有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Since the epoxy resin curing agent in the room temperature curing system is modified according to the general method, the prepared adhesive is highly active above 30 °C, and it is easy to produce "sudden polymerization" phenomenon during the construction process, resulting in waste of the adhesive and directly affecting the construction; or The activity is very poor, it is not easy to cure in 24 hours, which affects the construction period

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solidifying agent of epoxy resin for reinforcing and sealing, and method of preparing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] (1) Building and bridge reinforcement adhesive ratio (weight ratio)

[0054] CYD128 (epoxy resin) 100

[0055] EPG660 (reactive diluent) 15

[0056] Fumed silica (thickener) 1~3

[0057] This curing agent 45

[0058] Filler (silica powder, calcium carbonate, etc.) 15~30

[0059] KH-550 (coupling agent) 1

[0060] DMP-30 (accelerator) 0.5~1.5

[0061] Pigment (toner) 0.5~2.0

[0062] (2) Preparation method

[0063] Weigh CYD128, EPG660 and fumed silica according to the formula, stir well, then add filler, KH-550, stir well, finally add this curing agent, DMP-30 and pigment, stir well and proceed to construction.

Embodiment 2

[0065] (1) Proportion of sealing adhesive (weight ratio)

[0066] CYD128 (epoxy resin) 50

[0067] E-44 (epoxy resin) 50

[0068] EPG660 (reactive diluent) 5

[0069] Fumed silica (thickener) 1~4

[0070] This curing agent 50

[0071] Filler (silica powder, calcium carbonate, etc.) 0~50

[0072] KH-550 (coupling agent) 1

[0073] DMP-30 (accelerator) 0.5~1.5

[0074] Pigment (toner) 0~2

[0075] (2) Preparation method

[0076] Weigh CYD128, E-44, EPG660, fumed silica according to the ratio, stir evenly, then add filler, KH-550, stir evenly, finally add this curing agent, DMP-30 and pigment, stir well and carry out sealing and bonding .

[0077] 3. Effect verification

[0078] According to the mechanical performance test (shown in the table below) of the building and bridge reinforcement adhesive prepared according to embodiment 1

[0079] The table uses this curing agent to prepare the mechanical properties of building and bridge reinforcement adhesives

[0080]

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an epoxy resin curing agent for reinforcing and sealing, and a preparation method thereof, relating to an epoxy resin curing agent. The product is an environment friendly epoxy resin curing agent which is suitable for high temperature construction environment. The curing agent consists ofcomprises the main ingredients with the following weight percent: 70 to 76 percent of 4, 4'-diaminodiphenyl methane and 24 to 30 percent of polyphenyl polyamino methane, and the accessory ingredients with the following weight percent: 45 to 55 percent of thinner, 1 to 10 percent of catalyst and 5 to 40 percent of diepoxide. The invention uses the normal-pressure reaction method carries outfor synthesis through using normal-pressure reaction method, which avoids dangers of high-temperature and high-pressure synthesis. The product is free of 'three wastes'. The synthesis rate is 100 percent. The product has no obvious irritating odor and belongs to environment friendly products. The curing agent can solve the working life of the high-temperature construction in reinforcing and sealing fields in time because the curing agent has the advantages of is characterized in mild curing, good construction and high strength. The curing agent widens the application range of building reinforcement, bridge reinforcement and sealing fields.

Description

technical field [0001] The invention relates to an epoxy resin curing agent, in particular to an epoxy resin curing agent for reinforcement and sealing and a preparation method thereof. The product is an environment-friendly epoxy resin curing agent suitable for high-temperature construction environments. Background technique [0002] The invention of epoxy resin has gone through a long historical period. In 1947, the Devoe-Raynolds Company of the United States produced epoxy resin with industrial production value for the first time. Soon the Swiss Ciba company, the American Shell company and the De Chemical company all started the industrial production and application development of epoxy resin. The development of epoxy resin in my country began in 1956, and it was first successful in Shenyang and Shanghai. Industrial production began in Shanghai in 1958. After more than 40 years of struggle, the production and application of epoxy resin in my country has developed rapid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G59/50
Inventor 胡高平
Owner 湖北湖大资产经营有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com