Propylphenoxy compound with three-branch aromatic structure, preparation method thereof, and bismaleimide resin modified therewith

A technology of bismaleimide resin and propylene phenoxy, which is applied in the preparation of carbon-based compounds, organic compounds, chemical instruments and methods, etc., can solve the problem of high curing temperature and post-curing temperature, and poor thermal aging and other problems, to achieve the effect of reducing the curing reaction temperature and time, small mass loss, and reducing the activation energy of the reaction

Active Publication Date: 2017-01-04
INST OF PETROCHEM HEILONGJIANG ACADEMY OF SCI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims to solve the problem that the existing bismaleimide resin has high curing temperature and post-curing temperature during curing, and the problem of poor long-term thermal aging at high temperature after curing, and provides a three-branched aromatic structure. Oxygen compound and its preparation method and bismaleimide resin modified by it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Propylphenoxy compound with three-branch aromatic structure, preparation method thereof, and bismaleimide resin modified therewith
  • Propylphenoxy compound with three-branch aromatic structure, preparation method thereof, and bismaleimide resin modified therewith
  • Propylphenoxy compound with three-branch aromatic structure, preparation method thereof, and bismaleimide resin modified therewith

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0025]Specific embodiment 1: The general structural formula of a three-branched aromatic structure propenylphenoxy compound in this embodiment is:

[0026]

[0027] The R 1 for

[0028] The R 2 -H, -CH 3 、-OCH 3 or -CF 3 .

[0029] The propenylphenoxy compound of the three-branched aromatic structure in this specific embodiment is mainly tris(2-propenyl-5-methoxyphenoxy-4'-benzoyl)benzene, and its structural formula is:

[0030]

specific Embodiment approach 2

[0031] Embodiment 2: The preparation method of a three-branched aromatic structure propenylphenoxy compound described in this embodiment is carried out according to the following steps:

[0032] Mix the trifunctional fluoroketone and allylphenol to obtain the mixture, then add the mixture and the catalyst to the solvent, then raise the temperature of the reaction system to 150°C-205°C, and reflux at 150°C-205°C for 5h-8h , to obtain a crude product, filter the crude product, add ice water dropwise to the filtrate to cool the filtrate to a temperature of 0°C to 5°C, and precipitate at a temperature of 0°C to 5°C for 3h to 5h, finally filter and wash with water until The pH value of the washing solution is neutral, and the washed product is dried to obtain an alkenylphenoxy compound with a three-branched aromatic structure;

[0033] The molar ratio of the trifunctional fluoroketone to allylphenol is 1:(3~3.8); the molar ratio of the trifunctional fluoroketone to the catalyst is ...

specific Embodiment approach 3

[0034] Embodiment 3: The difference between this embodiment and Embodiment 2 is that the trifunctional fluoroketone is

[0035]

[0036] The allyl phenol is Others are the same as in the second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides propenyl phenoxy compounds with a three-branch aromatic structure and a preparation method thereof, and a bismaleimide resin modified by the propenyl phenoxy compounds, relating to the field of thermosetting resins and adhesives for high-temperature-resistant composite materials. The invention aims to solve the problems of higher curing temperature and higher after-treatment temperature in the existing bismaleimide resin and the problem of poor long-time thermal aging resistance of the cured resin at high temperature. The structural general formula is disclosed in the specification. The preparation method comprises the following steps: adding trifunctional fluoro ketone, allyl phenol and a catalyst into a solvent, heating to react under reflux, filtering, cooling, precipitating, washing with water and baking. The bismaleimide resin modified by the propenyl phenoxy compounds is prepared from bismaleimide, propenyl phenoxy compounds with three-branch aromatic structure, and diallylphenyl compounds. The invention mainly discloses a propenyl phenoxy compounds with three-branch aromatic structure and a preparation method thereof, and a bismaleimide resin modified by the propenyl phenoxy compounds.

Description

technical field [0001] The invention relates to the field of thermosetting resins and adhesives for high temperature resistant composite materials. Background technique [0002] Thermosetting resins are widely used in aerospace, electronics and electrical fields. Bismaleimide (BMI) is a typical representative of high-performance thermosetting resins. As a matrix resin, it plays an important role in the fields of composite materials and structural adhesives. It has the advantages of good mechanical properties, heat resistance, heat and humidity resistance, solvent resistance, etc., and its service temperature can reach as high as 232°C. Therefore, bismaleimide has become the main bearing force of aerospace above the service temperature of epoxy resin The material is resin. [0003] However, bis-horse resin is generally polymerized by diallyl bisphenol A and N,N'-4,4'-diphenylmethane bismaleimide, and the usual curing temperature is above 200°C, which is due to its curing Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07C45/64C07C49/84C07C41/16C07C43/285C07C315/04C07C317/22C08G73/12C09J179/08
CPCC07C41/16C07C43/285C07C45/64C07C49/84C07C315/04C07C317/22C08G73/12C08G73/125C08G73/127C09J179/08C09J179/085
Inventor 刘长威曲春艳王德志冯浩王海民宿凯
Owner INST OF PETROCHEM HEILONGJIANG ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com