A kind of nickel base gas valve alloy and preparation method thereof

A technology for alloys and valves, which is applied in the field of nickel-based valve alloys and its preparation, can solve the problems that materials cannot meet the needs, and achieve the effects of improving intergranular corrosion resistance, reducing production costs, and long service life at high temperatures

Active Publication Date: 2017-07-07
JIANGSU SHENYUAN SPECIAL STEEL +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to provide a novel nickel-based gas valve alloy to obtain a gas valve with excellent comprehensive performance, meet the requirements of the working conditions of advanced engines (internal combustion engines), and solve the problem that the materials of the prior art cannot meet the needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nickel base gas valve alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Example 1, a nickel-based gas valve alloy, the chemical composition is based on weight percentage, containing Ni: 55%, Cr: 20%, C: 0.03%, Al: 1.9%, Ti: 2.4%, W: 1.2%, Nb : 1.3%, Mo: 1.2%, Y: 0.09%, Hf: 0.12%, B: 0.004%, S≤0.02%, P≤0.02%, O≤0.02%, N≤0.02%, the balance is Fe and not Impurities to avoid, said impurity content ≤ 0.5%.

Embodiment 2

[0029] Example 2, a nickel-based gas valve alloy, the chemical composition is based on weight percentage, containing Ni: 60%, Cr: 25%, C: 0.02%, Al: 1.7%, Ti: 2.3%, W: 1.4%, Nb : 1.5%, Mo: 1.0%, Y: 0.08%, Hf: 0.08%, B: 0.004%, S≤0.02%, P≤0.02%, O≤0.02%, N≤0.02%, the balance is Fe and not Impurities to avoid, said impurity content ≤ 0.5%.

Embodiment 3

[0030] Embodiment 3, a nickel-based gas valve alloy, the chemical composition according to weight percentage, contains Ni: 58%, Cr: 23%., C: 0.04%, Al: 1.8%, Ti: 2.6%, W: 1.0%, Nb: 1.4%, Mo: 1.1%, Y: 0.1%, Hf: 0.06%, B: 0.003%, S≤0.02%, P≤0.02%, O≤0.02%, N≤0.02%, the balance is Fe and Unavoidable impurities, said impurity content ≤ 0.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses nickel-based air valve alloy. The nickel-based air valve alloy comprises 55.0 to 60.0% of Ni, 20.0 to 25.0% of Cr, 0.01 to 0.05% of C, 1.0 to 3.0% of Al, 1.0 to 3.0% of Ti, 0.5 to 1.5% of W, 0.5 to 1.5% of Nb, 0.5 to 1.5% of Mo, 0.05 to 0.20% of Y, 0.05 to 0.20% of Hf, 0.001 to 0.005% of B, not greater than 0.02% of S, not greater than 0.02% of P, not greater than 0.02% of O, not greater than 0.02% of N, and the balance of Fe and inevitable impurities, wherein the impurity content is not greater than 0.5%. The preparation method comprises the steps of sensing and melting under a vacuum condition; casting an electrode; remelting electroslag; thermally forging; locally modifying and grinding a quadrate ingot blank; thermally rolling; compensating temperature online; thermally rolling a steel wire rod. The nickel-based air valve alloy has high-temperature durability, high-temperature oxidation resistance, high wearability and high-temperature corrosion resistance.

Description

technical field [0001] The invention relates to a metal material and a preparation method thereof, in particular to a nickel-based gas valve alloy and a preparation method thereof. Background technique [0002] Valve steel has experienced multiple development stages such as carbon steel and low alloy steel ─ ─ silicon chromium stainless steel ─ а phase alloy ─ austenitic heat-resistant steel. In recent decades, the rapid development of engine (internal combustion engine) technology, such as: gasoline engine direct injection technology, variable valve timing technology, variable intake pipe, combustion rate control slide, variable displacement technology, high pressure common rail direct injection diesel engine etc., the load is higher than before, which makes the working temperature of the valve steel increase, the pressure is increased, the gas corrosion is serious, the reciprocating motion of the valve cone surface accelerates the wear, and the working conditions of the va...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C19/05
Inventor 朱治愿宫友军戴安伦张国付沈国平张竞涂玉国翟德建魏伟
Owner JIANGSU SHENYUAN SPECIAL STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com