Low-titanium-content double-layer covering agent for silicon steel and use method of low-titanium-content double-layer covering agent

A technology of covering agent and silicon steel, which is applied in the field of metallurgy, can solve the problems of increasing titanium in molten steel, and achieve the effects of improving the magnetic properties of finished products, stabilizing control, and reducing Ti sources

Active Publication Date: 2017-06-27
BEIJING SHOUGANG CO LTD
View PDF9 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the actual production process, it is found that the titanium content in the covering agent has a significant impact on the titanium composition in the molten steel during the casting process. However, due to the high content of silicon and alum

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-titanium-content double-layer covering agent for silicon steel and use method of low-titanium-content double-layer covering agent
  • Low-titanium-content double-layer covering agent for silicon steel and use method of low-titanium-content double-layer covering agent
  • Low-titanium-content double-layer covering agent for silicon steel and use method of low-titanium-content double-layer covering agent

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0083] The preparation method of the covering agent includes: mixing the materials of the above-mentioned components according to the weight ratio, and crushing until the average particle size is 1-10mm; or first crushing each material until the average particle size is 1-10mm, and then pressing The weight ratio is mixed evenly.

[0084] Such as figure 1 As shown, the embodiment of the present invention is used for the use method of the low-titanium double-layer covering agent of silicon steel, and described method comprises the following steps:

[0085] 1) When the weight of molten steel in the tundish reaches 1 / 8-1 / 4 of the normal casting weight, add 35-55kg of lower layer covering agent to the molten steel surface; when the weight of molten steel in the tundish reaches 1 / 3-2 of the normal casting weight / 3, add 60-80kg of lower layer covering agent to the molten steel surface;

[0086] 2) When the molten steel in the tundish reaches the normal casting weight, after the li...

Embodiment 1

[0091] Embodiment 1 of the present invention is a special low-titanium double-layer covering agent for high-grade silicon steel, including an upper layer covering agent and a lower layer covering agent, wherein the chemical composition and weight percentage of the upper layer covering agent are: SiO 2 45%, MgO 5%, CaO 6%, Fe 2 o 3 4%, Al 2 o 3 22%, C (full) 0.4%, TiO 2 ≤0.2%, the remainder is loss on ignition; the chemical composition and weight percentage of the lower covering agent are: SiO 2 16%, MgO 5%, CaO 56%, Fe 2 o 3 4%, Al 2 o 3 0.6%, C (full) 0.4%, TiO 2 0.12%, the balance is loss on ignition.

[0092] Embodiment 1 of the present invention is used for the use method of the low-titanium double-layer covering agent of silicon steel, and described method comprises the steps:

[0093] 1) When the weight of the molten steel in the tundish is 1 / 6, add the lower covering agent, add 25kg of the lower covering agent to the temperature measurement sampling hol...

Embodiment 2

[0099] Embodiment 2 of the present invention is a special low-titanium double-layer covering agent for high-grade silicon steel, including an upper layer covering agent and a lower layer covering agent, wherein the chemical composition and weight percentage of the upper layer covering agent are: SiO 2 53%, MgO 7%, CaO 7%, Fe 2 o 3 4%, Al 2 o 3 30%, C (full) 0.7%, TiO 2 0.34%, the balance is loss on ignition; the chemical composition and weight percentage of the lower layer covering agent are: SiO 2 21%, MgO 6%, CaO 61%, Fe 2 o 3 7%, Al 2 o 3 0.6%, C (full) 0.6%, TiO 2 0.08%, the balance is loss on ignition.

[0100] Embodiment 2 of the present invention is used for the use method of the low-titanium double-layer covering agent of silicon steel, and described method comprises the following steps:

[0101] 1) When the weight of molten steel in the tundish is 1 / 8, start to add the lower layer covering agent, respectively add 20kg of the lower layer covering agen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a low-titanium-content double-layer covering agent for silicon steel and a use method of the low-titanium-content double-layer covering agent. The low-titanium-content double-layer covering agent comprises an upper layer covering agent part and a lower layer covering agent part; the lower layer covering agent part is contacted with molten steel; the upper layer covering agent part is located above the lower layer covering agent part; the upper layer covering agent part comprises the following raw materials, by weight percentage, 44-62% of SiO2, 2-10% of MgO, 1-10% of CaO, greater than 0 and less than or equal to 7% of Fe2O3, 20-38% of Al2O3, greater than 0 and less than or equal to 1% of C (all), greater than 0 and less than or equal to 0.5% of TiO2, and the balance ignition lost; and the lower layer covering agent part comprises the following raw materials, by weight percentage, 15-25% of SiO2, 3-8% of MgO, 48-68% of CaO, 2-10% of Fe2O3, greater than 0 and less than or equal to 1% of Al2O3, greater than 0 and less than or equal to 1% of C (all), greater than 0 and less than or equal to 0.2% of TiO2, and the balance ignition loss. With the use of the low-titanium-content double-layer covering agent, the content of titanium in molten silicon steel can be reduced effectively.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, in particular to a low-titanium double-layer covering agent for silicon steel and its application method. Background technique [0002] With the maturity of the trinity smelting process of primary smelting-refining-continuous casting in the modern iron and steel industry, the tundish covering agent, as one of the important components, is mainly used to cover the surface of molten steel in the tundish during the continuous casting process. The basic requirements are: No adverse reaction with molten steel to avoid contamination of molten steel; no corrosion of alkaline tundish lining. Its main functions are: heat preservation of molten steel, avoiding excessive temperature drop of molten steel in the tundish during pouring and cold steel on the surface of molten steel, forming a liquid slag layer covering the surface of molten steel to isolate air and preventing secondary oxidation of molten ste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22D11/111
Inventor 赵艳宇彭开玉刘珍童胡卫东李志军刘建斌闵常杰张远芬
Owner BEIJING SHOUGANG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap