A kind of composite forward osmosis membrane and preparation method thereof

A composite technology of forward osmosis membrane and graphene, which is applied in the field of composite forward osmosis membrane and its preparation, can solve the problems of inaccessibility and low flux of forward osmosis membrane

Active Publication Date: 2021-03-12
BAOSHAN IRON & STEEL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the performance of the forward osmosis membrane obtained by this method is stronger than that of the commercial membrane CTA membrane, the thickness of the dense layer is still as high as 1-2 microns, which makes the flux of the forward osmosis membrane lower. mol L -1 When NaCl salt solution is used as the extraction solution, its water flux is only 7LMH, which still cannot meet the requirements of practical application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite forward osmosis membrane and preparation method thereof
  • A kind of composite forward osmosis membrane and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Dissolve 1g of isopropylacrylamide monomer and 1g of N,N-methylene bisacrylamide monomer in 20g of water, add 0.2g of sodium persulfate as an initiator; then add 0.1g of flake graphene to obtain the final precursor solution. And coating the nylon membrane with micron pores by spin coating, then heating at 70oC for two hours, and repeating the two steps of coating and heat treatment three times to obtain the final forward osmosis membrane.

[0027] figure 2 It is the scanning electron microscope (SEM) figure of the surface and the cross-section of the made forward osmosis membrane, a) the intercepting layer surface, b) the composite membrane cross-section; from which we can see that the surface of the membrane is uniform and dense, no leaks are seen, It can be seen from the cross-sectional view of the membrane that the thickness of the selective layer of the membrane is very thin, about 100 nanometers.

[0028] The test results of the water flux and salt rejection rat...

Embodiment 2

[0030] A film was prepared in a method similar to that of Example 1, except that the mass of graphene flakes was changed to 1.4 g, and a film with a similar structure was obtained.

[0031] The test results of the water flux and salt rejection rate of the membrane show that when using 1mol L -1 The NaCl solution is used as the extraction solution, the water flux of the membrane is 23.0LMH, and its reverse salt flux is 1.2g m -2 h -1 .

Embodiment 3

[0033] Adopt the method similar to embodiment 1 to make film, just change the quality of flake graphene into 0.05g, obtain the film with similar structure.

[0034] The test results of the water flux and salt rejection rate of the membrane show that when using 1mol L -1 The NaCl solution is used as the extraction solution, the water flux of the membrane is 25.9LMH, and its reverse salt flux is 1.5g m -2 h -1 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite forward osmosis membrane and a preparation method thereof, wherein the forward osmosis membrane is composed of a composite layer of a polymer and graphene and a highly porous substrate sublayer, and the polymer is composed of isopropylacrylamide monomer and N,N-methylenebisacrylamide monomer through free radical polymerization, the highly porous substrate is a porous aromatic polymer film; the mass ratio of the two monomers is 1:9-9:1, the mass of the graphene is 2.5%-70% of the mass of the copolymer. The preparation method includes the steps of precursor solution preparation, film coating and heat treatment. The forward osmosis membrane has very high water flux and salt rejection.

Description

technical field [0001] The invention relates to the technical field of membranes, in particular to a composite forward osmosis membrane and a preparation method thereof. Background technique [0002] Forward osmosis is a concentration-driven membrane technology, which refers to the transfer process of water from a high water chemical potential area to a low water chemical potential area through a selectively permeable membrane. It has the advantages of high recovery rate, less concentrated water discharge, low membrane fouling, and no external pressure, so forward osmosis technology has attracted more and more attention. In the process of commercialization of forward osmosis water treatment system, lack of suitable forward osmosis membrane is the most important technical obstacle restricting its large-scale development. [0003] The Netherlands "Journal of Membrane Science" (Journal of Membrane Science 360 ​​(2010) 522–535) reported a method for preparing a forward osmosis ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/40B01D71/02B01D69/12B01D69/02B01D67/00
Inventor 王焕庭金晟柱乔治·西蒙
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com