A kind of ultra-high strength magnetic yoke steel and its manufacturing method

An ultra-high-strength, manufacturing method technology, applied in the field of ultra-high-strength yoke steel and its manufacturing, can solve the problem of low strength, lack of magnetic properties of yoke steel, and inability to meet high-strength and good magnetic properties of generators in high-head hydropower stations requirements and other issues to achieve high strength, good magnetic induction performance, and improve the effect of tissue strengthening.

Active Publication Date: 2020-02-18
武汉钢铁有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The patent application number is 201610867421.3 The invention patent records "a CSP process to produce 1000MPa grade hot-rolled martensitic steel and its production method", its tensile strength can reach more than 1000MPa, but its yield strength is only about 800MPa, its strength is low At 900MPa, and does not have the magnetic properties required by the yoke steel
[0005] None of the above invention patents can meet the requirements of high strength and good magnetic properties of high head hydropower generators, so research and development are urgently needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-high strength magnetic yoke steel and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-10

[0021] The chemical composition (wt%) of the ultra-high-strength yoke steel described in Examples 1-10 is specifically shown in Table 1.

[0022] Table 1

[0023] Element C mn Si P S als Ti Nb Mo B N Example 1 0.10 1.96 0.02 0.015 0.006 0.05 0.21 0.7 0.55 0.003 0.006 Example 2 0.14 1.90 0.06 0.013 0.004 0.07 0.28 0.05 0.35 0.001 0.005 Example 3 0.12 1.95 0.03 0.012 0.006 0.10 0.24 0.07 0.40 0.002 0.006 Example 4 0.15 1.86 0.15 0.011 0.008 0.02 0.28 0.07 0.45 0.002 0.005 Example 5 0.11 1.98 0.10 0.012 0.005 0.03 0.23 0.06 0.49 0.003 0.008 Example 6 0.15 1.94 0.08 0.010 0.010 0.08 0.30 0.06 0.37 0.001 0.005 Example 7 0.11 1.86 0.03 0.012 0.006 0.05 0.22 0.05 0.40 0.002 0.005 Example 8 0.12 1.87 0.15 0.011 0.008 0.04 0.21 0.06 0.42 0.003 0.004 Example 9 0.11 1.92 0.10 0.012 0.005 0.03 0.24 0.06 0.50 0.003 0.006 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses super high strength magnet yoke steel. The super high strength magnet yoke steel comprises, by weight percentage, 0.10-0.15% of C, smaller than or equal to 0.15% of Si, 1.85-2.00% of Mn, smaller than or equal to 0.015% of P, smaller than or equal to 0.010% of S, 0.20-0.30% of Ti, 0.05-0.07% of Nb, 0.35-0.55% of Mo, 0.001-0.003% of B, 0.02-0.10% of Als, smaller than or equalto 0.010% of N and the balance Fe and inevitable impurities. According to the super high strength magnet yoke steel, in order to further improve strength and effectively break through the extreme strength 700 MPa of steel of a ferritic structure, in a structure reinforcing manner, by adding a proper amount of bainite to form elements, in cooperation with a super fast cooling process, a bainite structure is obtained, and the super high strength magnet yoke steel is obtained.

Description

technical field [0001] The invention relates to the field of micro-alloyed steel manufacturing, in particular to an ultra-high-strength magnetic yoke steel and a manufacturing method thereof. Background technique [0002] China's hydropower and coal energy reserves are roughly at the same level, and hydropower resources are clean, non-polluting, and renewable resources. Therefore, the development of hydropower construction has great practical significance for alleviating my country's power shortage and achieving sustainable development. According to my country's hydropower development plan, the future development potential in the Tibet region is huge, and according to the unique topography of the Tibet region, the hydropower stations built are all high-head hydropower stations, so the yield strength of the steel used for the rotor yoke part of the hydroelectric generator is required Further increase to more than 900MPa, but also requires good magnetic properties. [0003] Be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C21D8/12
CPCC21D8/1222C21D2211/002C22C38/001C22C38/002C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14
Inventor 宋畅胡唐国毛新平陶文哲毛传军陈吉清徐进桥刘昌明高智平
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com