Marbleized quartzite plate and preparation method thereof

A quartz stone plate and marble pattern technology, applied in the field of home improvement building materials manufacturing, can solve the problems of low product hardness, complex and cumbersome preparation process, poor strength, etc., and achieve the effects of excellent products, overcoming complex process and good toughness.

Inactive Publication Date: 2019-04-23
SUZHOU COZY HOUSE EQUIP
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation process of the current quartz stone products is complex and cumbersome, and the prepared products have low hardness and poor strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Marbleized quartzite plate and preparation method thereof
  • Marbleized quartzite plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The preparation of embodiment 1 quartz stone mixture

[0029] The components and the content of each component in the marble pattern mixture and the board main mixture are basically the same, the difference is only in the addition of pigments.

[0030] In parts by weight, the quartz stone mixture includes the following components:

[0031] Acrylic resin 5-20 parts, quartz sand 65-80 parts, silane coupling agent 0.1-5 parts, curing agent 0.1-5 parts, pigment 0-5 parts, fiber 1-20 parts. The above materials are common commercially available materials.

[0032] Quartz sand is made of quartz stone or silica powder with a particle size of 40-3000 mesh.

[0033] The silane coupling agent is γ-(methacryloxypropyl)trimethoxysilane, γ-(2,3-epoxypropoxy)propyltrimethoxysilane, N-β(aminoethyl)- γ-Aminopropylmethyldimethoxysilane, N-(β-aminoethyl)-γ-aminopropyltriethoxysilane, N-β(aminoethyl)-γ-aminopropyltrimethoxy ylsilane, anilinomethyltriethoxysilane, γ-aminopropyltriethoxy...

Embodiment 2

[0043] Embodiment 2 The preparation of the quartzite plate material imitating marble pattern

[0044] The preparation of the marble-like quartz stone plate in the present embodiment is carried out according to the following steps:

[0045] Step S1: Style Design

[0046] Design the color of the body of the slab and the color and texture of the marbling in the quartz stone slab. The color of the board body in this embodiment is black, and the color of the marble pattern is white.

[0047] Step S2: Prepare the mold

[0048] Prepare a pattern mold and a quartz stone plate mold according to the style of the quartz stone plate designed in step S1.

[0049] Step S3: Prepare materials

[0050]According to the style of the quartz stone plate designed in step S1, the marble pattern mixture and the main body mixture of the plate are prepared.

[0051] The preparation process in this embodiment is carried out according to the formula and preparation method described in Example 1.

...

Embodiment 3

[0059] The marble pattern mixture in this embodiment includes the following components: 20 parts of acrylic resin, 65 parts of quartz sand, 1 part of silane coupling agent, 3 parts of curing agent, 3 parts of white pigment, and 8 parts of fiber.

[0060] The board main compound includes the following components: 20 parts of acrylic resin, 65 parts of quartz sand, 1 part of silane coupling agent, 3 parts of curing agent, 3 parts of black pigment, and 8 parts of fiber.

[0061] The silane coupling agent in this embodiment is γ-(methacryloxypropyl) trimethoxysilane and / or γ-(2,3-glycidoxy)propyltrimethoxysilane, curing agent Di(4-tert-butyl)cyclohexyl peroxydicarbonate and / or dilauroyl peroxide.

[0062] The preparation method is the same as in Example 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a marbleized quartzite plate. The preparation method comprises the following steps of 1, style design, wherein colors of a plate main body in the quartzite plate and colors and textures of marbling are designed; 2, mold preparation, wherein a texture mold and a quartzite plate mold are prepared; 3, material preparation, wherein a marbling mixture anda plate main body mixture are prepared; 4, texture laying, wherein the texture mold is put into the quartzite plate mold, and the marbling mixture is laid into the texture mold; 5, main body laying,wherein the texture mold is taken out, and the plate main body mixture is laid into the quartzite plate mold to remove other portions of the marbling mixture; and 6, mold pressing, wherein after the surface is scraped to be level, the quartzite plate mold with materials laid therein is pressurized, heated and cured to be molded, so that the marbleized quartzite plate is obtained. A product obtained through the preparation method of the marbleized quartzite plate is stable and excellent in quality.

Description

technical field [0001] The invention relates to the technical field of home decoration building materials manufacturing, in particular to a method for preparing a marble-like quartz stone plate and the marble-like quartz stone plate prepared according to the preparation method. Background technique [0002] As a substitute for natural stone, artificial quartz stone has incomparable advantages over natural stone, such as high strength, high temperature resistance, corrosion resistance, anti-aging, easy cleaning, wear resistance, and no radiation. Artificial quartz stone plates are now available As a decorative material, it is widely used in industrial production and people's daily life. However, the preparation process of the current quartz stone product is complex and cumbersome, and the prepared product has low hardness and poor strength. Contents of the invention [0003] In view of this, in order to overcome the defects of the prior art, one of the purposes of the pres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B28B3/00B28B1/29C04B26/06C04B111/54
CPCB28B1/29B28B3/00C04B26/06C04B2111/545C04B2201/30C04B2201/50C04B14/06C04B24/42C04B2103/54C04B20/0048C04B24/045C04B24/008C04B24/121C04B24/00
Inventor 胡福涛
Owner SUZHOU COZY HOUSE EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap