Novel 3D (three-dimensional) printed protective material in high-negative-Poisson-ratio interwoven structure

A protective material, 3D printing technology, applied in the direction of additive processing, etc., to achieve good attenuation characteristics, good vibration and sound insulation performance, and excellent large deflection deformation ability

Active Publication Date: 2019-05-31
伊诺维(无锡)新材料科技有限公司
View PDF12 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, direct 3D printing of negative Poisson's ratio materials has not yet been achieved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel 3D (three-dimensional) printed protective material in high-negative-Poisson-ratio interwoven structure
  • Novel 3D (three-dimensional) printed protective material in high-negative-Poisson-ratio interwoven structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] refer to figure 1 , use 3D-printable common material (silica gel) with good tensile properties on the straight line, use bisphenol F epoxy acrylate resin (containing thinner TPGDA, photoinitiator BDK) for triangular nodes, and use CAD to precisely design Produce the structure (the design parameter is that the center distance of the circumscribed circle of the triangle is 10mm, and the side lengths of the triangle are respectively 1mm, 2.5mm, and 4mm), and use 3D printing technology to form a complete composite structure with a high negative Poisson's ratio structure; finally By using ABAQUS software to test its mechanical properties, it is concluded that the Poisson's ratio of the high negative Poisson's ratio structure combined with shape memory materials can reach -0.6, and it has high specific strength, large specific modulus, and good fatigue resistance. The tensile strength is high, but at the same time the elongation at break has a certain decrease. At the same ti...

Embodiment 2

[0027] refer to figure 1 , use 3D-printable ordinary materials (rubber) with good tensile properties in the straight line, pentaerythritol triacrylate resin is used in the triangle nodes, and the structure is precisely designed by using CAD (the diameter of the inscribed circle of the triangle is 10mm, 15mm, 20mm ,), use 3D printing technology (object's connex series) to form a complete composite structure with a high negative Poisson's ratio structure at the same time; finally, use ABAQUS software to test its mechanical properties, and get the shape memory The Poisson's ratio of the high negative Poisson's ratio structure combined with materials can reach -0.6.

[0028] The pentaerythritol triacrylate resin uses toluenesulfonic acid as a catalyst, adopts a polymerization inhibitor PMT, a decolorizing agent TSJ-1, and the amount of the catalyst is 4% of the quality of pentaerythritol, and the addition of the polymerization inhibitor is 4% of the quality of acrylic acid. The c...

Embodiment 3

[0031] In the same way as in Example 2, the present embodiment adopts the modified octadecyl acrylate at the triangular node, which is the monomer octadecyl acrylate, crosslinking agent propoxylated neopentyl glycol diacrylate and diluted The photoinitiator is prepared by reacting under the action of a photoinitiator; the photoinitiator is a benzoin ether-sulfur salt initiator (6wt%); the mass ratio of the monomer to the crosslinking agent is 1:0.18.

[0032] By using ABAQUS software to test its mechanical properties, it is concluded that the Poisson's ratio of the high negative Poisson's ratio structure combined with the shape memory material can reach -0.53.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel 3D printed protective material in a high-negative-Poisson-ratio interwoven structure. The novel 3D printed protective material in the high-negative-Poisson-ratio interwoven structure is printed and formed from shape memory materials and common rubber through droplet injection additive manufacturing. The structure of the novel 3D printed protective material in the high-negative-Poisson-ratio interwoven structure is internally provided with triangular structures (1), of which nodes are connected through linear structures (3); the neighboring linear structures (3)define unclosed hexagonal structures. By means of the 3D printing technology, improved photosensitive materials can be 3D-printed by temperature stimulus into objects with excellent memory, response,resilience, anti-seismic and adaptive properties and the like.

Description

technical field [0001] The invention relates to the technical field of protective materials, in particular to a novel 3D printed protective material with a high negative Poisson's ratio interwoven structure. Background technique [0002] At present, negative Poisson's ratio materials have been used in safety protection. Chinese utility model patent specifications CN206336247U and CN206782464U respectively disclose a car energy-absorbing box filled with a negative Poisson's ratio structure and an energy-absorbing anti-fall packing box based on a negative Poisson's ratio material. These two patents are protective materials made of energy-absorbing properties of negative Poisson's ratio materials. But the problem is that it is difficult to achieve a high negative Poisson's ratio (NP<-0.5), the reason is not only the structure, but also the material for making a high negative Poisson's ratio structure; [0003] At present, it is difficult to 3D print a soft material with a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08F291/02C08F222/14C08F220/18B33Y70/00B33Y80/00
Inventor 肖学良胡雨洁方镁淇贺燕贺录祥王鸿鹏
Owner 伊诺维(无锡)新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com