Highly transparent polished ceramic thick plate and preparation method thereof

A ceramic and transparent technology, applied in the field of high-transparency polished ceramic slabs and their preparation, can solve the problems of easy damage in forming and conveying, and achieve the effects of rich patterns, thick colors and crystal clear textures.

Active Publication Date: 2022-04-12
MONALISA GRP CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the increase of the specifications of ceramic products, when the strength of the green body is low, it is easy to be damaged in the process of forming and conveying

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Highly transparent polished ceramic thick plate and preparation method thereof
  • Highly transparent polished ceramic thick plate and preparation method thereof
  • Highly transparent polished ceramic thick plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 4

[0168] Example 4 is basically the same as Example 1, except that the composition of the raw material formula of the top glaze is shown in Table 10. The raw material formula of described surface glaze is shown in Table 25.

[0169] The surface glaze formula composition unit of table 25 embodiment 4: gram

[0170]

[0171] Surface glaze chemical composition analysis of table 26 embodiment 4

[0172]

[0173] On the basis of the surface glaze formula of the original formula B, the content of silicon, aluminum, and zirconium is increased, and the firing temperature of the surface glaze is correspondingly increased, which effectively solves defects such as prickly heat and pinholes on the brick surface during the production process. question.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
surface areaaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a highly transparent polished ceramic thick plate and a preparation method thereof. The preparation method of the highly transparent polished ceramic slab comprises the following steps: using the green body powder to prepare a high-strength full-body ceramic thick slab green body, the strength of the green body is 2.8-3.5MPa; applying a top glaze on the green body, the The amount of glaze applied to the surface glaze is 520-580g / m 2 ; Apply high transparent dry granule glaze, the glazing amount of the dry granule glaze is 800~850g / m 2 ; Firing at a temperature of 1200-1290° C. for 75-180 minutes; making large-scale ceramic thick plates.

Description

technical field [0001] The invention relates to a highly transparent polished ceramic thick plate and a preparation method thereof, belonging to the technical field of ceramic tile production and manufacture. Background technique [0002] With the increase of the specifications of ceramic products, when the strength of the green body is low, it is easy to be damaged in the process of forming and conveying. The present invention is committed to developing a new type of ceramic thick plate that is different from traditional large plates. The thick plate can be drilled, polished, and cut more conveniently. It is suitable for various shapes. It is positioned as a high-end household application product and can meet The flexible application in different occasions puts forward great requirements on the body, strength, random cutting, surface effect and product design of ceramic tiles. Contents of the invention [0003] In view of the above problems, the present invention provide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/34C04B41/89C03C8/00C03C8/04
CPCC04B33/13C04B33/34C04B41/89C04B41/52C03C8/00C03C8/04C04B2235/3217C04B2235/656C04B2235/6567C04B41/50C04B41/5022
Inventor 谢志军欧阳成黄玲艳卢海鹏黄秋立肖伟荣
Owner MONALISA GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com