A technology of grinding aid and triethanolamine, which is applied in the field of cement production grinding aids, can solve the problems that the expected use effect cannot be achieved and the cost of grinding aids is high, and can improve the grinding process, improve the flow rate of materials, and eliminate static electricity in the mill. Effect
Pending Publication Date: 2020-06-09
XINJIANG TIANSHAN CEMENT CO LTD
View PDF4 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The cost of existing grinding aids in the mark
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] A self-made grinding aid, its raw material components are as follows: ethylene glycol: 8kg, triethanolamine: 15kg, glycerin residue: 15kg, sodium acetate: 1kg, industrial salt: 1kg, lignin: 2kg, water: 58kg.
[0020] Its preparation method is as follows:
[0021] Step 1: Control the temperature of water at 40°C during preparation, add glycerin residue and triethanolamine and mix evenly;
[0022] Step 2: In step 1, add glycerin residue and triethanolamine to the water and mix evenly, then add ethylene glycol, sodium acetate, lignin, and industrial salt in sequence.
Embodiment 2
[0024] A self-made grinding aid, its raw material components are as follows: ethylene glycol: 10kg, triethanolamine: 20kg, glycerin residue: 20kg, sodium acetate: 1.5kg, industrial salt: 1kg, lignin: 2.5kg, water: 45kg.
[0025] Its preparation method is as follows:
[0026] Step 1: Control the temperature of water at 42°C during preparation, add glycerin residue and triethanolamine and mix evenly;
[0027] Step 2: In step 1, add glycerin residue and triethanolamine to the water and mix evenly, then add ethylene glycol, sodium acetate, lignin, and industrial salt in sequence.
Embodiment 3
[0029] A self-made grinding aid, its raw material components are as follows: ethylene glycol: 12kg, triethanolamine: 25kg, glycerin residue: 25kg, sodium acetate: 1.5kg, industrial salt: 1.5kg, lignin: 3kg, water: 32kg.
[0030] Its preparation method is as follows:
[0031] Step 1: Control the temperature of water at 43°C during preparation, add glycerin residue and triethanolamine and mix evenly;
[0032] Step 2: In step 1, add glycerin residue and triethanolamine to the water and mix evenly, then add ethylene glycol, sodium acetate, lignin, and industrial salt in sequence.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a self-made grinding aid. The raw material components are as follows: 10-15% of ethylene glycol, 20-35% of triethanolamine, 20-30% of glycerol residues, 1-5% of sodium acetate,1-2% of industrial salt, 1-3% of lignin and the balance water (totaling 100%). The preparation method comprises the following steps: step 1, during preparation, controlling the temperature of water to be 40-45 DEG C, adding the glycerol residues and the triethanolamine, and then uniformly mixing the glycerol residues and the triethanolamine; and step 2, adding glycerol residues and triethanolamine into water, and uniformly mixing, and sequentially adding ethylene glycol, sodium acetate, lignin and industrial salt. The self-made grinding aid can solve the problem of low yield of a mill in thecement production process, the clinker ratio is high, static electricity in the mill is eliminated, a cement grinding process is improved, the grinding efficiency is improved, and the production costof the cement grinding aid is reduced; the cement grinding table yield can be effectively increased by 5-7 tons/hour, the clinker ratio is reduced by 2.0%, the power consumption is reduced by 1.5-2 kilowatts/ton, and meanwhile, various chemical and physical inspection results of cement meet the national standard.
Description
technical field [0001] The invention relates to the field of grinding aids for cement production, in particular to a self-made grinding aid. Background technique [0002] Adding additional liquid that meets the national requirements in the cement production process can improve the grinding efficiency of cement, reduce the comprehensive power consumption of cement production, increase the production of cement units, and can effectively improve the strength of cement. At the same time, the ground cement meets the requirements of national standards. Analysis The performance and function of the raw materials required for self-made grinding aids, while ensuring that the addition of cement will not affect the performance of cement. [0003] The cost of existing grinding aids in the market is high, and the expected use effect cannot be achieved. Contents of the invention [0004] The object of the present invention is to provide a kind of self-made grinding aid, to solve the pro...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more