Heat-sensitive Mn-Zn ferrite series material combined synthesis and high throughput screening method

A heat-sensitive manganese-zinc and screening method technology, which is applied in the direction of inorganic material magnetism, can solve the problems that the series of bulk heat-sensitive ferrite magnetic materials have not been reported at home and abroad, and achieve low cost, high efficiency and high efficiency Effect

Inactive Publication Date: 2005-06-22
SHANGHAI JIAOTONG UNIV +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] So far, the application of combinatorial synthesis and high-throughput screening technology to develop a series of bulk thermosensitive ferrite magnetic materials has not been reported at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-sensitive Mn-Zn ferrite series material combined synthesis and high throughput screening method
  • Heat-sensitive Mn-Zn ferrite series material combined synthesis and high throughput screening method
  • Heat-sensitive Mn-Zn ferrite series material combined synthesis and high throughput screening method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0049] In the embodiment of the present invention, according to figure 1 The process shown, using combinatorial synthesis and high-throughput screening technology, carried out the specific development and screening of heat-sensitive manganese-zinc ferrite series materials, and completed and established the -40°-+160°C temperature in less than half a year. For the material library within the range, the Curie temperature interval is 2°C, the material permeability μ>2000, the maximum slope of the μ-T curve is greater than 145 / °C, and the μ-T characteristics are excellent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Curie pointaaaaaaaaaa
Curie pointaaaaaaaaaa
Login to View More

Abstract

A combinatorial synthesis and high-throughput screening method for thermosensitive manganese zinc ferrite series materials, the target is a practical thermosensitive material with a magnetic permeability μ > 2000 and excellent μ-T characteristics within the temperature range of -40°-+160°C Manganese zinc ferrite series magnetic materials, through different material formulas and preparation processes, establish a sample material library, use a computer-controlled μ-T characteristic test system to analyze and obtain library characterization, and establish a database of sample composition-preparation process-physical properties , After collecting and sorting, conduct primary selection of materials, conduct further analysis and research and optimize, screen out leading materials, and then carry out large-scale trial production. The high-throughput combination design, preparation and screening method of the present invention not only has high efficiency and low cost, but also can greatly shorten the cycle of developing new materials, and is especially suitable for preparing multi-component complex mixtures and serial compounds, so as to obtain a large number of new materials Or materials with excellent performance.

Description

Technical field: [0001] The invention relates to a combined synthesis and high-throughput screening method for heat-sensitive manganese-zinc ferrite series materials, that is, a method for efficiently developing heat-sensitive MnZn ferrite series materials by using combined synthesis and high-throughput screening technologies. Background technique: [0002] Combinatorial synthesis and high-throughput screening technology originated from the combinatorial chemistry technology proposed by H.Geysen et al. in the 1980s. Subsequently, in the process of developing new drugs, combinatorial chemistry and high-throughput synthesis and screening technologies were further developed, which greatly accelerated the development process of new drugs. In the field of new drug discovery, annual screening of 1 million different compounds was achieved in 1999, and the R&D cost of each lead drug was reduced by about two orders of magnitude. [0003] In 1995, Dr. Xiang Xiaodong and Professor P.G...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/38H01F1/10
Inventor 刘公强王锦辉薛祥荣蔡金华郭刘
Owner SHANGHAI JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products