Corn fiber and regenerative hemp fiber blended antibacterial composite yarn and producing method thereof

A technology of corn fiber and hemp fiber, applied in yarn, textile and paper making, etc., can solve the problems of poor wearability, low moisture absorption, poor spinnability, etc.

Inactive Publication Date: 2009-12-23
JIANGSU FUTENG TEXTILE +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to overcome the deficiencies in the prior art, provide a corn fiber that can take advantage of the advantages of good luster, high strength, good elasticity, high modulus, and biodegradability, and make up for its low moisture absorption and poor spinnability. , no natural antibacterial properties, poor taking performance and other shortcomings, but also under the premise of maintaining the antibacterial, moisture absorption, breathable and cool advantages of hemp fiber, the high strength and good shape retention of corn fiber make up for the hemp fiber. The fiber has the disadvantages of poor drapability and poor shape retention, and can spin fine-gauge yarns, even extra-fine-gauge yarns below 10tex, which overcomes the problem that hemp fibers are difficult to spin fine-gauge yarns

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corn fiber and regenerative hemp fiber blended antibacterial composite yarn and producing method thereof
  • Corn fiber and regenerative hemp fiber blended antibacterial composite yarn and producing method thereof
  • Corn fiber and regenerative hemp fiber blended antibacterial composite yarn and producing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A production method for blending antibacterial composite yarn of 14.5tex corn fiber and regenerated hemp fiber. The blending ratio is: 60 parts of corn fiber and 40 parts of regenerated hemp fiber. The detailed steps of the process are as follows. The regenerated hemp fiber can be made from one or more of hemp short hemp, hemp drop, hemp stalk and rod core.

[0054] 1. Process flow:

[0055] Corn fiber: A002D bale opener→A035D mixed opener (with condenser)→A035D mixed opener (with condenser)→A036B porcupine opener (with condenser)→A092A cotton feeder (with condenser) Condenser)→A076F lapping machine→FA201B carding machine

[0056] Regenerated hemp fiber: A002D bale opener → A035D mixed opener (with condenser) → A035D mixed opener (with condenser) → A036B porcupine opener (with condenser) → A092A cotton feeder ( Condenser attached)→A076F lapping machine→FA201B carding machine

[0057] Corn fiber raw sliver and regenerated hemp fiber raw sliver→FA311 (FA303) draw frame...

Embodiment 2

[0071] A production method of 14.5tex corn fiber and regenerated hemp fiber blended antibacterial composite yarn, the blending ratio is: corn fiber accounts for 50 parts, regenerated hemp fiber accounts for 50 parts, and the detailed steps of the process are as follows. The regenerated hemp fiber can be made from one or more of hemp short hemp, hemp drop, hemp stalk and rod core.

[0072] 1. Process flow:

[0073] Same as Example 1

[0074] 2. Spinning process parameters

[0075] (1) Corn fiber opening and cleaning, carding, pre-merging process

[0076] Same as Example 1

[0077] (2) Regenerated hemp fiber opening and cleaning, carding, pre-merging process

[0078] Same as Example 1

[0079] (3) Drawing process

[0080]

[0081]

[0082] (4) Roving process: roving basis weight is 3.13g / 10m, roving twist coefficient is 85, rear area draft is 1.17 times, total draft is 8.24 times, roller center distance is 52×54mm, roller pressure is 26×15× 22N.

[0083] (5) Spinni...

Embodiment 3

[0085] A production method of 14.5tex corn fiber and regenerated hemp fiber blended antibacterial composite yarn, the blending ratio is: corn fiber accounts for 30 parts, regenerated hemp fiber accounts for 70 parts, and the detailed steps of the process are as follows.

[0086] 1. Process flow:

[0087] Same as Example 1

[0088] 2. Spinning process parameters

[0089] (1) Corn fiber opening and cleaning, carding, pre-merging process

[0090] Same as Example 1

[0091] (2) Regenerated hemp fiber opening and cleaning, carding, pre-merging process

[0092] Same as Example 1

[0093] (3) Drawing process

[0094]

[0095] (4) Roving process: the roving weight is 4.022g / 10m, the roving twist coefficient is 75, the rear draft is 1.24 times, the total draft is 7.73 times, the roller center distance is 52×54mm, and the roller pressure is 26×14× 14N.

[0096] (5) Spinning process: the front roller speed is 220r / min; the twist coefficient is 330; the nip gap is 3.0mm; the rea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
twist factoraaaaaaaaaa
twist factoraaaaaaaaaa
Login to View More

Abstract

An antibacterial composite yarn blended with corn fiber and regenerated hemp fiber and a production method thereof relate to spinning technology. According to the technical solution provided by the present invention, the antibacterial composite yarn includes 30-60 parts of corn fiber and 40-70 parts of regenerated hemp fiber; One or more fibers made from recycled raw materials. During manufacturing: a. Go through the corn fiber in sequence: opening and cleaning, carding, and pre-merging processes for later use; b. Process the regenerated hemp fiber in sequence: opening and cleaning, carding, and pre-merging processes for later use; c. The pre-combined corn fiber and regenerated hemp fiber are sequentially subjected to drawing, roving, spun yarn and winding processes to obtain corn fiber and regenerated hemp fiber blended antibacterial composite yarn. The invention combines the excellent characteristics of high strength and good shape retention of corn fiber fabrics, makes up for the shortcomings of poor drape and shape retention of hemp fiber and regenerated hemp fiber fabrics, and can spin fine yarns, which overcomes the difficulty of spinning hemp fibers No. yarn problem.

Description

technical field [0001] The invention relates to an antibacterial composite yarn made by blending corn fiber and regenerated hemp fiber and discloses a production method of the composite yarn. Background technique [0002] The development of new biodegradable fibers for clothing fabrics or industrial textiles is one of the important topics in the development and research of textiles today. Corn fiber is a new type of environmentally friendly fiber developed by Cargill-Dow (CARGILL~DOW) Polymer Company and Japan Bell Spinning and other companies. The fiber is made of polylactic acid fiber extracted from corn starch, that is, PLA fiber, which is called corn fiber in our country. [0003] Corn fiber combines the advantages of natural fiber and chemical fiber. Its mechanical properties are between polyester and nylon, and its strength and modulus are lower than polyester fibers and higher than nylon. Therefore, corn fiber fabrics are soft to the touch, have silky luster and br...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More