3104Aluminum alloy spectral standard sample and preparation method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A spectral standard sample and aluminum alloy technology, which is applied in the field of aluminum alloy standard sample and its preparation, can solve the problems that cannot accurately control and determine the chemical composition, affect the improvement of product process and the improvement of product quality, etc.
Active Publication Date: 2008-07-02
SOUTHWEST ALUMINUM GRP
View PDF0 Cites 16 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The previously developed 3000 series standard samples only contain eight elements, Si, Fe, Cu, Mn, Mg, Zn, Ti, and Ni, but do not contain four elements, Na, Pb, Cd, and Ga, so it is impossible to accurately control and determine the tank material Use the chemical composition of Pb, Cd, Na, and Ni in 3104 aluminum alloy to affect the improvement of the product process, the improvement of product quality and the needs of the product
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0014] Example 1 E6301 aluminum alloy standard spectrum sample
[0015] Aluminum contains the following elements by weight:
[0016] Si 0.65±0.05%, Fe 0.84±0.06%, Cu 0.03±0.01%, Mn 0.70±0.05%, Mg 1.48±0.1%, Zn 0.05±0.01%, Ti 0.05±.01%, Ni 0.006±.001%, Cd 3±1ppm, Pb 160±10ppm, Ga 0.010±0.002%, V 0.10±0.01%, and Na 1ppm.
Embodiment 2
[0017] Example 2 E6302 aluminum alloy standard spectrum sample
[0018] Aluminum contains the following elements by weight:
[0019] Si 0.50±0.05%, Fe 0.65±0.05%, Cu 0.10±0.01%, Mn 0.82±0.05%, Mg 1.28±0.1%, Zn 0.12±0.01%, Ti 0.9±0.01%, Ni 0.02±0.005%, Cd 15 ±5ppm, Pb 130±10ppm, Ga 0.030±0.002%, V 0.075±0.005%, and Na 5ppm.
Embodiment 3
[0020] Example 3 E6303 aluminum alloy standard spectrum sample
[0021] Aluminum contains the following elements by weight:
[0022] Si 0.35±0.03%, Fe 0.50±0.04%, Cu 0.17±0.02%, Mn 0.95±0.05%, Mg 1.09±0.10%, Zn 0.20±0.01%, Ti 0.13±0.01%, Ni 0.06±0.01%, Cd 30 ±5ppm, Pb 100±10ppm, Ga 0.055±0.005%, V 0.055±0.005%, and Na 10ppm.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a 3104 aluminum alloy spectrum standard sample, which is characterized in that the aluminum comprises Si 0.04-0.70%, Fe 0.18-0.90%, Cu 0.02-0.34%, Mn 0.65-1.3%, Mg 0.65-1.58%, Zn 0.04- 0.34%, Ti 0.04-0.91%, Ni 0.05-0.11%, Cd 2-70ppm, Pb 8- 170ppm, Ga 0.008-0.11%, V 0.008-0.11% and Na 1-40ppm. The invention also discloses a preparation method thereof. The inventive aluminum alloy spectrum standard sample can be used for the control and the analysis of 3104 aluminum alloy.
Description
technical field [0001] The invention relates to an aluminum alloy standard sample and a preparation method thereof, which are used for analyzing and controlling elements in 3000 series aluminum alloys. Background technique [0002] In order to meet the needs of environmental protection and improve the quality of aluminum products used in medicine and food packaging, the requirements for the chemical composition of 3104 aluminum alloys for can materials are more stringent, except for the elements required by ordinary 3104 alloys (Si, Fe, Cu, Mn, Mg, Zn , Ti, Ga and V), also require: Pb≤0.008%, Cd≤0.002%, Pb+Cd≤0.009%, Na≤0.0004%, Ni≤0.05%. The previously developed 3000 series standard samples only contain eight elements, Si, Fe, Cu, Mn, Mg, Zn, Ti, and Ni, but do not contain four elements, Na, Pb, Cd, and Ga, so it is impossible to accurately control and determine the tank material Using the chemical composition of Pb, Cd, Na, and Ni in 3104 aluminum alloy will further affec...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more