Air conditioner foils and method for preparing same

A technology for air-conditioning foil and raw materials, applied in the field of aluminum product processing, can solve problems such as changing the composition, and achieve the effects of fine organization, favorable thickness reduction, and excellent comprehensive performance.

Inactive Publication Date: 2010-12-22
SHANGHAI DATUN ENERGY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to meet the market's requirements for the performance of air-conditioning aluminum foil, it is impossible to only change the production process, so it is necessary to continuously change the composition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An air-conditioning foil and a preparation method thereof, which are made of the following raw materials in parts by weight:

[0018] 0.25 parts of iron, ≤0.15 parts of silicon, 0.20 parts of manganese, 0.02 parts of titanium, and 80 parts of aluminum.

[0019] An air-conditioning foil and a preparation method thereof according to claim 1, comprising the steps of:

[0020] (1) Put the high-grade aluminum ingots into the feeding barrel, put the aluminum ingots into the smelting furnace with a crane, ignite and heat until the aluminum ingots soften and collapse, then stop the fire and stir;

[0021] (2) Sprinkle the covering agent on the above-mentioned uniformly stirred raw materials, continue to ignite and heat to 760°C, and mix according to the requirements of the above-mentioned alloy element content;

[0022] (3) The iron element is added in the form of aluminum-iron master alloy, the manganese element is added in the form of manganese agent, and the titanium elemen...

Embodiment 2

[0028] An air-conditioning foil and a preparation method thereof, which are made of the following raw materials in parts by weight:

[0029] 0.30 parts of iron, ≤0.15 parts of silicon, 0.25 parts of manganese, 0.06 parts of titanium, and 90 parts of aluminum.

[0030] An air-conditioning foil and a preparation method thereof according to claim 1, comprising the steps of:

[0031] (1) Put the high-grade aluminum ingots into the feeding barrel, put the aluminum ingots into the smelting furnace with a crane, ignite and heat until the aluminum ingots soften and collapse, then stop the fire and stir;

[0032] (2) Sprinkle the covering agent on the above-mentioned uniformly stirred raw materials, continue to ignite and heat to about 760°C, and mix according to the requirements of the above-mentioned alloy element content;

[0033] (3) The iron element is added in the form of aluminum-iron master alloy, the manganese element is added in the form of manganese agent, and the titanium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention relates to foils with alloying component proportioning and a method for making the same, in particular to aluminum foils used for the production of a radiator of an air conditioner and a method for making the same, belonging to the aluminum product processing field. The invention aims to overcome the defects existing in the prior art and provide air conditioner foils which are made by elements of iron, manganese, silicon, titanium and aluminum with the optimized component proportioning through processes of cast-rolling, cold-rolling and annealing; the aluminum foils have the advantages of compact structure and excellent comprehensive performance, and particularly facilitate the reduction of thickness and lower manufacturing costs; moreover, the aluminum foils can realize that air conditioner fins are not broken when the fins undergo the high-speed punching, thereby meeting market requirements.

Description

technical field [0001] The invention relates to a foil with an alloy composition ratio and a preparation method thereof, in particular to an aluminum foil suitable for producing air-conditioning radiator fins and a preparation method thereof, belonging to the field of aluminum product processing. Background technique [0002] With the development of modern market economy, the fierce competition in the air conditioner market and the narrowing of profit margins are becoming more and more obvious. Reducing the cost of air conditioner fin aluminum foil and improving the forming efficiency are the focus of air conditioner manufacturers. Therefore, research and development of thin and high-performance air-conditioning foil products is the main trend of air-conditioning foil technology progress. [0003] The development of air-conditioning foil has undergone many changes. The first is the thickness, from the initial 0.2mm to 0.12-0.16mm in the 1980s, 0.10-0.115mm in the 1990s, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00B23P15/00
Inventor 曾凡炯雷银娥徐静霞
Owner SHANGHAI DATUN ENERGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap