Process for preparing bamboo pulp cotton

A preparation process, the technology of bamboo pulp cotton, applied in the direction of coating, etc., can solve the problems of non-degradable, increased environmental pollution, difficult recycling, etc., and achieve the effect of convenient and extensive materials, long-term and excellent antibacterial and antibacterial effects, and rich bamboo resources

Active Publication Date: 2012-10-17
JIAXING JEHONN CLEANING PRODS
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Traditional cleaning sponges use hydrophilic PVA collodion and some EVA sponges, but these sponges have great defects: they cannot be degraded, recycling is difficult, and their raw materials are also dependent on petroleum products, so their use has great limitations sex, will increase environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1. Dipping

[0023] Temperature: 30° C., time: 60 minutes, sodium hydroxide concentration: 18 wt%.

[0024] 2. Mature

[0025] Temperature: 40°C, time 5 hours.

[0026] 3. Yellowing

[0027] Initial temperature 20-22°C; final temperature 24-26°C; time 120 minutes, carbon disulfide (relative to methyl fiber): 33-35wt%.

[0028] 4. Post-dissolution

[0029] Temperature: 12-14°C, time: 3 hours.

[0030] 5. Sponge preparation

[0031] Maturity ammonium chloride value: 7.0ml, sodium sulfate decahydrate weight / viscose weight=1:3, coloring agent is 0.5‰ of viscose weight.

[0032] 6. Sponge forming

[0033] Temperature: 70°C, time 5-8 hours.

[0034] 7. Treatment after cleaning

[0035] Wash 1-3 times with water at 40-60°C to remove most of the sodium sulfate decahydrate in the sponge. Then carry out pickling, acid bath temperature: 50°C, acid bath sulfuric acid concentration 50g / l. After pickling, carry out desulfurization, and then carry out alkali washing, the te...

Embodiment 2

[0037] 1. Dipping

[0038] Temperature: 35° C., time: 60 minutes, sodium hydroxide concentration: 18 wt%.

[0039] 2. Mature

[0040] Temperature: 40°C, time 5 hours.

[0041] 3. Yellowing

[0042] Initial temperature 20-22°C; final temperature 24-26°C; time 120 minutes, carbon disulfide (relative to methyl fiber): 33-35wt%.

[0043] 4. Post-dissolution

[0044] Temperature: 12-14°C, time: 3 hours.

[0045] 5. Sponge preparation

[0046] Maturity ammonium chloride value: 7.5ml, sodium sulfate decahydrate weight / viscose weight=1:4, coloring agent is 0.5‰ of viscose weight.

[0047] 6. Sponge molding

[0048] Temperature: 70°C, time 5-8 hours.

[0049] 7. Treatment after cleaning

[0050] Wash 1-3 times with water at 40-60°C to remove most of the sodium sulfate decahydrate in the sponge. Then carry out pickling, acid bath temperature: 50°C, acid bath sulfuric acid concentration 50g / l. After pickling, carry out desulfurization, and then carry out alkali washing, the te...

Embodiment 3

[0052] 1. Dipping

[0053] Temperature: 40° C., time: 60 minutes, sodium hydroxide concentration: 18 wt%.

[0054] 2. Mature

[0055] Temperature: 40°C, time 5 hours.

[0056] 3. Yellowing

[0057] Initial temperature 20-22°C; final temperature 24-26°C; time 120 minutes, carbon disulfide (relative to methyl fiber): 33-35wt%.

[0058] 4. Post-dissolution

[0059] Temperature: 12-14°C, time: 3 hours.

[0060] 5. Sponge preparation

[0061] Maturity ammonium chloride value: 6.5ml, sodium sulfate decahydrate weight / viscose weight=1:5, coloring agent is 0.5‰ of viscose weight.

[0062] 6. Sponge molding

[0063] Temperature: 70°C, time 5-8 hours.

[0064] 7. Treatment after cleaning

[0065]Wash 1-3 times with water at 40-60°C to remove most of the sodium sulfate decahydrate in the sponge. Then carry out pickling, acid bath temperature: 50°C, acid bath sulfuric acid concentration 50g / l. After pickling, carry out desulfurization, and then carry out alkali washing, the tem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a process for preparing bamboo pulp cotton, comprising the following steps of preparation of bamboo glue, preparation of a sponge and posttreatment. The process is characterized in that the bamboo glue is prepared by the steps of soaking bamboo fibers in an alkaline liquor, then ageing, yellowing and carrying out post-dissolution; the sponge is prepared by mixing ripened glue and sodium sulfate decahydrate, adding a colorant, evenly stirring, putting into an appointed mold and heating for curing and forming, wherein the ripening ammonium chloride value reaches 7+ / -0.5ml, and the weight of the sodium sulfate decahydrate is 3-5 times of the weight of the glue; and the posttreatment comprises the following steps of: washing the formed sponge 1-3 times to remove most of sodium sulfate decahydrate in the sponge, then carrying out acid-washing, desulfuring and alkali-washing, then washing to be neutral with tap water, and carrying out moisturizing and fungus-resisting treatment to obtain the finished product of the bamboo pulp cotton. The bamboo pulp cotton prepared by adopting the process disclosed by the invention is clean and environment-friendly and has durable antibiosis and bacteriostasis effects.

Description

technical field [0001] The invention relates to a production process of a sponge product using bamboo fiber as a raw material, in particular to a preparation process of bamboo pulp cotton, and the prepared sponge can be widely used in the cleaning field. Background technique [0002] Traditional viscose fiber is made of wood fiber and cotton fiber, and after a series of reaction processes, viscose short fiber, long fiber, cellophane and other products are prepared. [0003] Bamboo fiber is extracted from bamboo. Bamboo is a kind of rapid growth and abundant output. The use of bamboo fiber greatly reduces the need for wood fiber and cotton fiber, and reduces the damage to forest resources. Secondly, because bamboo fiber has special properties, the most prominent The most important thing is its antibacterial and bacteriostatic effect, and most of the antibacterial and bacteriostatic sponges at this stage are achieved by adding bactericidal and antifungal agents, and this type ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L1/24C08J9/26C08J9/36C08J9/40C08B9/00
Inventor 沈宇弘
Owner JIAXING JEHONN CLEANING PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap