RTM (Resin transfer molding) technology for composite material molding

A composite material and process technology, applied in the field of RTM molding process of composite materials, can solve the problems of long molding time and large deformation of products in RTM process, and solve the problems of long molding time, low production cost and long molding time. Effect

CN103240893AInactive Publication Date: 2013-08-14JIANGSU AOXIN NEW ENERGY AUTOMOBILE
2 Cites 8 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2013-08-14
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
Patent Text Reader

Abstract

The invention discloses an RTM (resin transfer molding) technology for composite material molding. The RTM technology for composite material molding comprises the following steps of: step one, placing glass fiber reinforcing materials in advance in a mold cavity of a mold; step 2, injecting a prepared resin glue solution into the mold cavity from an injection hole after a mold is closed and locked at certain temperature and pressure, and soaking the glass fiber reinforcing materials; and step 3, controlling the temperature and curing through a heating device in the mold, starting up the mold, and demolding. The RTM technology for composite material molding disclosed by the invention can effectively solve the problems of longer molding time as well as great product deformation in the prior art, and the technology is low in production cost, and is beneficial to popularization.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to an RTM forming process of composite materials, in particular providing a process in which a heating device for maintaining a specific temperature is arranged in a forming mold, and a temperature control technology is used to control the curing of composite material products. Background technique

[0002] RTM (Resin Transfer Molding) is the abbreviation of resin transfer molding. It originated from the cold mold casting process in the 1950s and has a history of more than 40 years, but the RTM process has really been valued by people and has developed rapidly only in the past ten years. Because this process has a series of advantages such as high efficiency, low investment, good working environment, low energy consumption, and strong process adaptability, it is very popular and develops rapidly. Has been widely used in construction, transportation, telecommunications, health, aerospace and other fields. The Japan Reinforced Pla...

Examples

Embodiment Construction

[0022] The present invention will be further described below in conjunction with accompanying drawing.

[0023] Embodiments of the present invention are described in detail below, examples of which are shown in the drawings, wherein the same or similar reference numerals designate the same or similar elements or elements having the same or similar functions throughout. The embodiments described below by referring to the figures are exemplary only for explaining the present invention and should not be construed as limiting the present invention.

[0024] Such as figure 1 - As shown in 2, inject materials A and B (resin system) into the mold cavity through the metering pump, infiltrate the reinforcing material (fiber system), and then close the mold and lock the prepared resin glue solution at 15°C - 35°C and 0.05 - Under the pressure of 0.25MPa, inject the mold cavity from the injection hole to saturate the glass fiber reinforced material; finally, after temperature-controll...