Anti-static GAG sheet and preparation method thereof

An antistatic and sheet technology, applied in chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve the problem that PET-GAG sheets are prone to static electricity, antistatic agents are not easy to retain, and affect development and use and other problems, to achieve the effect of high appearance transparency, permanent and effective antistatic value, and high thermal stability

Active Publication Date: 2014-07-02
郭鸣明 +1
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PET-GAG sheets are prone to static electricity, which affects its development and use.
At present, the conventional antistatic methods are external coating and internal antistatic agent. The external antistatic agent is not easy to retain, thus losing its antistatic property. Internal antistatic agent is easy to cause white spots or white spots on the appearance of the sheet. other defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] It is composed of 10% upper layer PETG, 80% middle layer APET and 10% lower layer PETG;

[0030] Among them: the upper layer of PETG is made of 20 parts of PETG resin, 2 parts of carbon nanotubes and 1 part of carbon nanofibers,

[0031] The middle layer APET consists of 93.2 parts of CZ318 polyester chips, 5 parts of nano silver-silica and 1.8 parts of nano CaCO 3 Made of particles,

[0032] The lower layer of PETG is made of 80 parts of PETG resin, 3 parts of antioxidant (phosphite) and 1 part of 4-methoxybenzylidene dimethyl malonate.

[0033] The preparation method is:

[0034] (1) Preparation of upper layer PETG

[0035] Dry the PETG resin at 65°C for 5 hours, add antioxidants and dimethyl 4-methoxybenzylidene malonate, and enter the SJ65 single-screw extruder through a vacuum feeder. The pressure is set at 4Mpa, the speed is 20 rpm, and the temperature of the extruder is 200 ℃ to plasticize, melt, and extrude; filter by the screen changer, pressurized by the melt pump, and ...

Embodiment 2

[0043] It is composed of 10% upper layer PETG, 80% middle layer APET and 10% lower layer PETG;

[0044] Among them: the upper layer of PETG is made of 30 parts of PETG resin, 2 parts of carbon nanotubes and 1 part of carbon nanofibers,

[0045] The middle layer APET consists of 93.2 parts of CZ318 polyester chips, 5 parts of nano silver-silica and 1.8 parts of nano CaCO 3 Made of particles,

[0046] The lower layer of PETG is made of 90 parts of PETG resin, 3 parts of antioxidant (phosphite) and 1 part of 4-methoxybenzylidene dimethyl malonate.

[0047] The preparation method of Example 2 is the same as the preparation method of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an anti-static GAG sheet and a preparation method thereof. The anti-static GAG sheet is formed by compositing an upper PETG layer, a middle APET layer and a lower PETG layer in a weight ratio of 10%, 80% to 10% respectively, wherein the upper PETG layer is made from PETG resin, carbon nano tubes and carbon nano fibers; the middle APET layer is made from CZ318-type PET chips, nano-silver-silica and nano CaCO3 particles; the lower PETG layer is made from PETG resin, antioxygen and 4-methoxy benzylidene malonic acid dimethyl ester. Under the condition that the product appearance of the prepared and obtained GAG sheet is not influenced, the resistance value can reach 10 to the power of 12 Omega.m, and the anti-static value is permanently effective; the prepared GAG sheet is high in appearance transparency, free of turbidity, crystal points or flow lines, and has high heat stability, impact strength and gas barrier property. The preparation method provided by the invention is reasonable in technology.

Description

Technical field [0001] The invention relates to an antistatic GAG sheet and a preparation method thereof. Background technique [0002] PET-GAG sheet is a composite sheet with outstanding toughness and high impact strength. Its impact strength is 3-10 times that of modified polyacrylates. It has a wide processing range and high mechanical strength. Strength and excellent flexibility. However, PET-GAG sheets are prone to static electricity, which affects its development and use. At present, the conventional antistatic method is two kinds of external coating and internal antistatic agent. The external antistatic agent is not easy to retain, thus losing its antistatic property. The internal antistatic agent is easy to cause white spots or white spots in the appearance of the sheet. Other defects. Summary of the invention [0003] In view of the shortcomings of the prior art, the purpose of the present invention is to provide an antistatic GAG sheet, through a reasonable raw materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/06B32B27/18B32B27/36
Inventor 王焕玉赵俊锋穆喜泽谭洪生王玉燕
Owner 郭鸣明
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com