A high-strength aluminum alloy material, aluminum alloy plate and manufacturing method thereof

A technology for aluminum alloy materials and aluminum alloy plates, which is applied in the fields of aluminum alloy materials, aluminum alloy plates and their manufacturing, can solve the problems of increasing yield strength and tensile strength, decreasing elongation, and springback of aluminum alloy plates.

Active Publication Date: 2017-02-22
BAOSHAN IRON & STEEL CO LTD
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, 6000 series Al-Mg-Si alloy materials will undergo natural aging after solution treatment, and magnesium and silicon atoms will segregate at room temperature, resulting in an increase in yield strength.
Especially in the process of transportation and storage of aluminum alloy plates, the mechanical properties of the plates will be unstable as time goes by, often the yield strength and tensile strength will increase, while the elongation will decrease significantly, resulting in the aging of aluminum alloys. The plate rebounds seriously during stamping, and even cracks during edge wrapping, which seriously affects product quality
In addition, the yield strength of 6000 series Al-Mg-Si alloy materials after painting and baking under conventional casting and rolling conditions is usually lower than 300MPa, which cannot meet the needs of the automotive industry for higher strength lightweight aluminum plate structures. piece of demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-strength aluminum alloy material, aluminum alloy plate and manufacturing method thereof
  • A high-strength aluminum alloy material, aluminum alloy plate and manufacturing method thereof
  • A high-strength aluminum alloy material, aluminum alloy plate and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

manufacture Embodiment A1-A8

[0075] see figure 1 , according to the following steps to manufacture the aluminum alloy plates in Examples A1-A8 and Comparative Examples B1-B2:

[0076] 1) Smelting: adding intermediate alloy and refining agent in molten aluminum water by conventional smelting method, and controlling the mass percentage ratio of each chemical element as shown in Table 1;

[0077] 2) Double-belt casting: cooling from the liquidus temperature (720°C) to the solidus temperature at a cooling rate of 100-500°C / s, and the thickness of the cast slab is 8-10mm;

[0078] 3) Cold rolling: the right turning roll 12 transports the slab to the work roll, and the slab is rolled by the work roll 14 of the rolling mill, and the cold rolling reduction rate is controlled to 70-90% to obtain a cold rolled slab with a thickness of 1 mm ;

[0079] 4) On-line solution treatment: The aluminum alloy plate is heated to 500-560° C. at a heating rate of 80-120° C. / s by the first on-line induction heating device 15a,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength aluminum-alloy material. The high-strength aluminum-alloy material contains the chemical elements in percentage by mass: not lower than 1.5% and not higher than 3.0% of Mg, not lower than 0.05% and not higher than 0.2% of Si, not lower than 0.1% and not higher than 0.2% of Mn, not lower than 0.2% and not higher than 0.4% of Fe, higher than 0 and not higher than 0.03% of Cu, higher than 0 and not higher than 0.05% of Ti, either not lower than 0.05% and not higher than 0.15% of Ca or not lower than 0.05% and not higher than 0.15% of Sr and the balance of Al and other unavoidable impurities. The invention further discloses an aluminum-alloy plate manufactured from the aluminum-alloy material. The invention further discloses a manufacturing method of the aluminum-alloy plate, wherein the method comprises the steps of carrying out double-strip casting, carrying out cold rolling, carrying out online solid solution treatment and carrying out online aging pretreatment. The high-strength aluminum-alloy material and the aluminum-alloy plate, disclosed by the invention, have relatively high strength and good natural aging stability. After painting and baking, the yield strength of the high-strength aluminum-alloy material and the aluminum-alloy plate is higher than 300Mpa.

Description

technical field [0001] The invention relates to an alloy material, in particular to an aluminum alloy material. The invention also relates to an aluminum alloy plate made of the aluminum alloy material and a manufacturing method thereof. Background technique [0002] Lightweight automotive materials is the focus of current automakers. The use of aluminum alloy sheets for the manufacture of automotive structural parts is also increasing, and the optional materials are 2000 series, 5000 series and 7000 series alloy materials. However, the corrosion resistance of Cu-containing 2000 series alloy materials is poor, 5000 series alloy materials are prone to softening during the baking process, and 7000 series alloy materials have insufficient elongation, which will cause difficulties in material processing. The 6000 series Al-Mg-Si alloy materials that can be strengthened by heat treatment are gradually being widely used due to their good formability, corrosion resistance and wel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/08C22F1/047
CPCC22C21/08C22F1/047
Inventor 徐世伟蒋浩民唐伟能张丕军
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com