Manufacturing method of optical fiber base material

一种制造方法、光纤母材的技术，应用在制造工具、玻璃制造设备、玻璃沉积炉等方向，能够解决非产品部分增大等问题

Active Publication Date: 2018-01-16
SHIN ETSU CHEM CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] In addition, in Patent Document 3, a method of changing the moving range of the reciprocating movement is proposed for each moving axis, but in this method, there is a problem of increasing the tapered non-product portions at both ends.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of optical fiber base material
  • Manufacturing method of optical fiber base material
  • Manufacturing method of optical fiber base material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] use as figure 1 , figure 2In the shown apparatus, a porous glass base material for an optical fiber is produced by an external vapor deposition method. As the starting part, dummy rods with an outer diameter of 50 mm and a length of 500 mm were welded to both ends of a mandrel with an outer diameter of 50 mm and a length of 3000 mm, and glass frit was deposited until the outer diameter reached 300 mm.

[0047] The burner uses a multi-nozzle type accumulation burner with a small-diameter combustion-supporting gas nozzle enclosed in a combustible gas outlet, and three burners are arranged at intervals of 150mm on both the A-axis and the B-axis.

[0048] Such as image 3 As shown, in order not to make the staggered positions of the burners on the A-axis and the B-axis overlap in the length direction of the starting part, as Figure 4 Set the movement speed of the A axis as shown, such as Figure 5 The movement speed of the B-axis was set as shown, and stacking was per...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Provided is an optical fiber base material manufacturing method that includes, while rotating a starting member formed by fusing both ends of a core rod to dummy rods on an axis of the starting member, moving the starting member and burners back and forth relative to each other and depositing glass microparticles on a surface of the starting member. This method also includes setting two or more axes as back and forth movement axes allowing for back and forth movement relative to the starting member; providing a burner facing the starting member on each of the axes; causing each burner to traverse the starting member to an end of the starting member; and changing a position where at least two burners pass by each other during the traversing movement, in a longitudinal direction of the starting member.

Description

technical field [0001] The present invention relates to a method for manufacturing an optical fiber preform capable of high speed and having a uniform thickness in the length direction of a starting part. Background technique [0002] Conventionally, various methods have been proposed for producing an optical fiber preform. In these methods, while rotating the starting member having dummy rods (Damilod) welded to both ends of the mandrel around the axis, the starting member and a plurality of burners are relatively reciprocated, and the surface of the starting member is The external vapor deposition method (OVD method) that accumulates glass particles, dehydrates and sinters them in an electric furnace to obtain an optical fiber base material, can obtain a relatively arbitrary refractive index distribution, and can mass-produce a large-diameter optical fiber base material, so being widely used. [0003] In this external vapor deposition method, studies have been made to in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B37/018
CPCC03B37/0142C03B2207/52C03B2207/64C03B2207/66C03B2207/70Y02P40/57
Inventor 吉田真
Owner SHIN ETSU CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com