Preparation method of chainlike ultralow-temperature magnetics coordination polymer material

A coordination polymer and ultra-low temperature technology, applied in chemical instruments and methods, luminescent materials, etc., to achieve good thermal stability

Inactive Publication Date: 2017-03-29
LIAONING UNIVERSITY OF PETROLEUM AND CHEMICAL TECHNOLOGY
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few studies on chain-like ultra-low temperature magnetic coordination polymers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of chainlike ultralow-temperature magnetics coordination polymer material
  • Preparation method of chainlike ultralow-temperature magnetics coordination polymer material
  • Preparation method of chainlike ultralow-temperature magnetics coordination polymer material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] MnCl 2 and aminotrimethylene phosphonic acid in a molar ratio of 1:1 were dissolved in 20 mL of deionized water, adjusted to a pH of 3-4 with 0.1 M KOH solution, then mechanically stirred for 3 h, and the mixed solution was packaged in a reaction kettle, 150 After heating at °C for 7 days and cooling to room temperature, massive crystals were precipitated to obtain the complex with a yield of 63%.

Embodiment 2

[0023] MnCl 2 and aminotrimethylene phosphonic acid in a molar ratio of 0.5:1 were dissolved in 10 mL of deionized water, adjusted to a pH of 3-4 with 0.1 MKOH solution, then mechanically stirred for 2 h, and the mixed solution was packaged in a reaction kettle at 140 ° C was heated for 5 d, cooled to room temperature, massive crystals were precipitated, and the yield was 55%.

Embodiment 3

[0025] MnCl 2 and aminotrimethylene phosphonic acid in a molar ratio of 0.5:1.5 were dissolved in 30 mL of deionized water, and the pH was adjusted to 3-4 with 0.1 MKOH solution, then mechanically stirred for 3 h, and the mixed solution was packaged in a reaction kettle, and the temperature was 150 ° C was heated for 6 d, cooled to room temperature, massive crystals were precipitated, and the yield was 60%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of magnetic properties and materials, in particular to a preparation method of a chainlike ultralow-temperature magnetics coordination polymer material, which mainly comprises the following steps: dissolving MnCl2 and amino trimethylene phosphonic acid into 10 to 30mL of deionized water according to the molar ratio of (0.5 to 1.5) : (0.5 to 1.5), adjusting pH to be 3 to 4 by using a 0.1M KOH solution, performing mechanical stirring for 2 to 4h, packaging a mixed solution in a reaction still, heating for 5 to 8d under the temperature of 140 to 160 DEG C, and cooling to room temperature, thus separating out bulk crystals. Preferably, the preparation method comprises the following steps: dissolving MnCl2 and amino trimethylene phosphonic acid into the deionized water according to the molar ratio of 1 to 1, adjusting the pH to be 3 to 4 by using the 0.1M KOH solution, then performing mechanical stirring for 3h, heating for 7d under the temperature of 150 DEG C, and cooling until the bulk crystals are separated out. The coordination compound provided by the invention has the characteristics of good heat stability, stable magnetic properties and fluorescence-emission property.

Description

technical field [0001] The invention relates to the field of magnetic properties and materials, in particular to a method for preparing a chain-like ultra-low temperature magnetic coordination polymer material. Background technique [0002] Existing studies on the magnetic properties of complexes mainly focus on ferromagnetic and antiferromagnetic transition metals and some elements in rare earth metals, and mainly test the magnetic susceptibility curve of the complexes with temperature. When the temperature drops to the Curie temperature Finally, the complexes show ferromagnetic or antiferromagnetic coupling, and the research in this area is relatively common. But there is still little research on chain-like ultra-low temperature magnetic coordination polymers. Contents of the invention [0003] The purpose of the present invention is to establish a material whose magnetic properties are controlled by temperature based on the magnetic properties of complexes. Expand the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G83/00C09K11/06
CPCC08G83/008C09K11/06C09K2211/188
Inventor 关磊王莹
Owner LIAONING UNIVERSITY OF PETROLEUM AND CHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap