A kind of super frost-resistant cement profile and preparation method thereof

A frost-resistance and cement technology, applied in the field of ultra-freeze-resistance cement profiles and their preparation, can solve the problems of reducing the water content of concrete and increasing the number of harmless pores, so as to reduce porosity, improve frost resistance, and improve Freezing effect

Inactive Publication Date: 2019-10-29
YANCHENG INST OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, none of the existing reports can significantly increase the number of harmless pores and reduce the water content of concrete. Therefore, it is impossible to fundamentally find a way to improve the frost resistance of concrete.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of super frost-resistant cement profile and preparation method thereof
  • A kind of super frost-resistant cement profile and preparation method thereof
  • A kind of super frost-resistant cement profile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be further described in detail below in combination with specific embodiments.

[0019] The components used in Examples 1-5 are shown in Table 1 (mass percentage), and the steel slag and slag used in the examples are all obtained from Baosteel Group Corporation.

[0020] Table 1

[0021]

[0022]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an ultra-frost-resistant cement profile and a preparation method thereof. The ultra-frost-resistant cement profile comprises the following components in percentage by mass: 50-100% of C3S2 cement, 0-40% of steel residues and 0-25% of ore slag. The preparation method comprises the following steps: (1) grinding and screening the C3S2 cement or a mixture of the C3S2 cement, the steel residues and the ore slag, controlling a water-ash ratio to be 0.19-0.35, and performing vibration molding so as to obtain a blank; (2) putting the blank into a reaction kettle with a CO2 gas, and performing a heating reaction, thereby obtaining the ultra-frost-resistant cement profile. The ultra-frost-resistant cement profile has calcium carbonate crystal of CO2 and calcium-containing minerals in blank pores, and along with increase of the reaction time, the pores are fully filled with the crystal, so that the porosity can be degraded, the number of harmless pores can be reduced, and the frost resistance of the cement can be improved.

Description

technical field [0001] The invention belongs to the field of building materials, in particular to a super frost-resistant cement profile and a preparation method thereof. Background technique [0002] Freeze-thaw damage is one of the main reasons for the damage of concrete, especially in low temperature and cold regions, due to the freezing and expansion of the solution in the pores, micro-crack damage occurs inside the concrete, and such damage gradually disappears under the action of multiple freeze-thaw cycles Accumulative expansion eventually leads to loosening and cracking inside the concrete. The essential factor of freeze-thaw damage is that the concrete contains pores and aqueous solution. According to the influence of different pore sizes on the performance of concrete, Wu Zhongwei, a famous scientist in my country, divides the pores in concrete into harmless pore levels. less harmful hole level Harmful hole level and Hazardous Hole and proposed to increase...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B40/02C04B111/20
CPCC04B28/04C04B40/0231C04B2111/29C04B18/142C04B18/141
Inventor 侯贵华张宏伟陈佳男许宁张勤芳曹月斌
Owner YANCHENG INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com