High-position bumper environment-friendly flame-retardant polyurethane foaming material and preparation method thereof

A technology of foaming materials and bumpers, which is applied in the field of environmentally friendly flame-retardant polyurethane foaming materials for high-position bumpers and its preparation, which can solve the problems of short escape time for personnel, difficult car body and people's protection, and unsatisfactory bumper strength. Effect and other issues

Inactive Publication Date: 2017-11-03
YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The strength of traditional bumpers usually cannot achieve ideal results. In the event of an accident, it is difficult to provide ideal protection for the body and people. Also, due to poor flame retardancy, the escape time of personnel is short, and there is a great potential safety hazard.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An environmentally friendly flame-retardant polyurethane foam material for a high-position bumper, comprising the following preparation steps: firstly, a composite material is prepared in parts by mass:

[0019] Polyester 330: 35 parts;

[0020] Polyester 3350: 25 parts;

[0021] Polyester 400: 9 parts;

[0022] Silicone oil: 2.5 parts;

[0023] Catalyst HPF1: 1.2 parts;

[0024] Catalyst S20: 1.0 parts;

[0025] Water: 3.0 parts;

[0026] Flame retardant TCPP: 33 parts.

[0027] Put the above materials into the reaction kettle for mixed reaction, wherein the silicone oil is silicone oil AK-158, the stirring speed is 130r / min, and the stirring time is 4h to obtain the combined material, and then the acetonitrile polyester and the combined material are mixed according to the ratio of 1:1.65 The mass ratio of the high-position bumper can be prepared by mixing the environmentally friendly flame-retardant polyurethane foam material.

Embodiment 2

[0029] An environmentally friendly flame-retardant polyurethane foam material for a high-position bumper, comprising the following preparation steps: firstly, a composite material is prepared in parts by mass:

[0030] Polyester 330: 40 parts;

[0031] Polyester 3350: 30 parts;

[0032] Polyester 400: 10.5 parts;

[0033] Silicone oil: 3 parts;

[0034] Catalyst HPF1: 1.65 parts;

[0035] Catalyst S20: 1.25 parts;

[0036] Water: 3.4 parts;

[0037] Flame retardant TCPP: 36 parts.

[0038] Put the above materials into the reaction kettle for mixed reaction, wherein the silicone oil is silicone oil AK-158, the stirring speed is 140r / min, and the stirring time is 4.5h to obtain the combined material, and then the acetonitrile polyester and the combined material are mixed according to 1: The mass ratio of 1.65 is uniformly mixed to obtain the environmentally friendly flame-retardant polyurethane foam material for the high-position bumper.

Embodiment 3

[0040] An environmentally friendly flame-retardant polyurethane foam material for a high-position bumper, comprising the following preparation steps: firstly, a composite material is prepared in parts by mass:

[0041] Polyester 330: 45 parts;

[0042] Polyester 3350: 30 parts;

[0043] Polyester 400: 10.5 parts;

[0044] Silicone oil: 3 parts;

[0045] Catalyst HPF1: 1.65 parts;

[0046] Catalyst S20: 1.25 parts;

[0047] Water: 3.4 parts;

[0048] Flame retardant TCPP: 36 parts.

[0049] Put the above materials into the reaction kettle for mixed reaction, wherein the silicone oil is silicone oil AK-158, the stirring speed is 150r / min, and the stirring time is 5h to obtain the combined material, and then the acetonitrile polyester and the combined material are mixed according to the ratio of 1:1.65 The mass ratio of the high-position bumper can be prepared by mixing the environmentally friendly flame-retardant polyurethane foam material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-position bumper environment-friendly flame-retardant polyurethane foaming material and a preparation method thereof. The high-position bumper environment-friendly flame-retardant polyurethane foaming material comprises the following components in percentage by mass: acetonitrile polyester and a combined material with the mass ratio being 1:1.65, wherein the combined material consist of the following components in parts by mass: 35 to 45 parts of polyester 330, 25 to 35 parts of polyester 3350, 9 to 12 parts of polyester 400, 2.5 to 3.5 parts of silicone oil, 1.2 to 1.8 parts of a catalyst HPF1, 1.0 to 1.5 parts of a catalyst S20, 3.0 to 3.8 parts of water and 33 to 39 parts of a flame retardant TCPP; the silicone oil is silicone oil AK-158; the components of the combined material are added into a reaction kettle to perform mixing reaction at the stirring speed being 130 to 150 r/min for 4 to 5 hours to obtain the combined material, the acetonitrile polyester and the combined material are mixed uniformly according to the mass ratio of 1:1.65 to prepare the high-position bumper environment-friendly flame-retardant polyurethane foaming material. By adoption of the materials and the method, the prepared high-position bumper environment-friendly flame-retardant polyurethane foaming material is flame-retardant and high-temperature resistant, has high flame retardance, high strength and long service life, and is environmentally friendly.

Description

technical field [0001] The invention relates to an environment-friendly flame-retardant polyurethane foam material for a high-position bumper and a preparation method thereof, belonging to the field of automobiles. Background technique [0002] At present, with the development of the automobile industry and the enhancement of people's awareness of safety and environmental protection, people's requirements for auto parts have also increased significantly. As a part of safety precautions, people have stricter requirements for bumpers. High temperature resistance, high flame retardancy, high strength, light weight, long service life, and high environmental protection characteristics. The strength of traditional bumpers usually cannot achieve ideal results. In the event of an accident, it is difficult to provide ideal protection for the body and people. Also, due to poor flame retardancy, the escape time of personnel is short, and there is a great potential safety hazard. . Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/42C08K5/521C08J9/08C08G101/00
CPCC08G18/4202C08K5/521C08G2110/0025C08G2110/0083
Inventor 朱章娣朱凌宇纪朝根
Owner YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap