Method for bending forming of windshield

A bending forming and windshield technology, which is applied in glass forming, glass reshaping, glass manufacturing equipment, etc., can solve the problems of low windshield processing efficiency, etc., and achieve good glass bending effect, strong practicability, and improved The effect of processing efficiency

Active Publication Date: 2018-02-09
CHONGQING SHUNHUA SAFETY GLASS CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention intends to provide a method for bending and forming windshields to solve the problem of low efficiency in the bending and forming of windshields in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for bending forming of windshield

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The present invention will be described in further detail below by means of specific embodiments:

[0020] The reference signs in the accompanying drawings of the description include: bending mold 1, vent hole 2, strut 3, air bag 4, vent chamber 5, first branch pipe 6, second branch pipe 7, third branch pipe 8, valve 9, air pipe 10, Support plate 11, glass 12, M-shaped air duct 13, flexible graphite film 14, marker pen 15.

[0021] The embodiment is basically as figure 1 Shown: a method for bending and forming a windshield of the present invention, comprising the following processing steps:

[0022] Step 1: Perform pretreatment on the windshield 12 raw material to be bent and formed, that is, cut it into required size.

[0023] Step 2: Prepare glass bending and forming equipment, including a hollow bending mold 1, the curved surface of the bending mold 1 is the working surface, a number of air holes 2 are provided on the curved surface of the bending mold 1, and two s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for bending forming of a windshield and belongs to the technical field of reforming primary glass. The method comprises the following processing steps: step one, carrying out pretreatment processing on glass; step two, preparing glass bending forming equipment; step three: introducing hot gas for softening the glass; step four, continuously introducing the hot gas, using an air bag to act on the glass, and enabling the glass to be bent and laminated on a bending die; step five, introducing cold gas and carrying out cooling forming treatment on the glass. According to the technical scheme, the problem that the windshield is low in processing efficiency of bending forming in the prior art is effectively solved; the method has the advantages of good glass bending effect, convenience for glass forming, high practicality and high processing efficiency.

Description

technical field [0001] The invention belongs to the technical field of reshaping of primary glass. Background technique [0002] In the past, in the case of bending windshields, the following processing method was mainly used: the windshield was cut into a predetermined size and shape, and it was placed on a bending mold installed in a heating furnace in an atmospheric environment. Heating to the softening temperature of the glass sheet that can be bent and shaped (it varies depending on the glass material, but generally around 550°C to 700°C), and then the flat glass is pulled by its own weight or clamped on both sides of the flat glass to make the flat glass Deforms to follow the shape of the curved die. [0003] However, the existing heating furnace is more common to heat the glass from bottom to top, resulting in uneven heating surface of the glass, resulting in longer heating time, wasting more energy, and low processing efficiency; It takes a long time to wait, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03B23/03
CPCC03B23/0352
Inventor 袁顺华
Owner CHONGQING SHUNHUA SAFETY GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap