A Forging Method for Improving the Grain Size of 15-5ph Stainless Steel

A technology of stainless steel and grain size, which is applied in the field of material processing, can solve the problems of easy growth of grains and achieve the effect of improving the reliability of the structure

Active Publication Date: 2020-04-07
SHAANXI HONGYUAN AVIATION FORGING
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of the above-mentioned situation of the prior art, the purpose of the present invention is to provide a kind of forging method that improves the grain size of 15-5PH stainless steel, to solve the problem that the grain grows easily when forging 15-5PH stainless steel, thereby ensure the forging strength, improve Tissue Reliability of 15-5PH Stainless Steel Components

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Forging Method for Improving the Grain Size of 15-5ph Stainless Steel
  • A Forging Method for Improving the Grain Size of 15-5ph Stainless Steel
  • A Forging Method for Improving the Grain Size of 15-5ph Stainless Steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1.1 Raw materials

[0027] (1) The chemical composition of the raw material of 15-5PH stainless steel billet was re-inspected according to the standard AMS 5659, and the result was qualified, see Table 1;

[0028] Table 1 Chemical Composition of Raw Materials

[0029]

[0030] (2) The mechanical properties of raw materials are re-inspected according to the standard AMS5659, and the result is qualified, see Table 2;

[0031] Table 2 Mechanical Properties of Raw Materials

[0032]

[0033] (3) Low-magnification structure of raw materials: no metallurgical defects, standard: AMS 5659;

[0034] (4) High-magnification structure of raw materials: no free ferrite, standard: AMS 5659;

[0035] (5) Raw material flaw detection: According to Φ2.0 flat bottom hole, the result is qualified, standard: A grade in AMS-STD-2154;

[0036] Grain size evaluation metallographic diagram of raw materials figure 2 shown.

[0037] 1.2 Forging, heat treatment and inspection

[0038...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a forging method for improving the grain size of 15-5PH stainless steel. Conventional forging forming is conducted on a 15-5PH stainless steel blank, and thus the blank is close to the forming size; according to the part shape, the blank obtained after conventional forging forming is bent, the forging preheating temperature of the blank is 850 DEG C+ / -50 DEG C, the heatingcoefficient is 0.2-0.3 min / mm, the forging heating temperature is 1000 DEG C-1150 DEG C+ / -15 DEG C, the heating coefficient is 0.3-0.4 min / mm, after heat preservation is conducted to the set time, the blank is taken out of a furnace immediately to be bent on a flat die hammer, and meanwhile the temperature is controlled; and the bent blank is subjected to heat treatment. According to the forgingmethod, the bending procedure of the forging blank is arranged to be completed at the heating number of finish forging, the forging heating temperature is lowered, and thus the problem that during small-deformation finish forging of the 15-5PH stainless steel, grains are liable to grown up is solved. Through the forging method, the strength, plasticity and fracture toughness of a 15-5PH stainlesssteel forge piece can reach the expected requirement, and the structure reliability of a 15-5PH stainless steel component is improved.

Description

technical field [0001] The invention belongs to the field of material processing, in particular to a forging method for improving the grain size of 15-5PH stainless steel. Background technique [0002] 15-5PH is a martensitic, precipitation hardening, chrome-nickel-copper stainless steel with good surface smoothness and dimensional stability. Good processing technology, excellent mechanical properties, and general corrosion resistance. 15-5PH steel has the characteristics of high strength, good transverse toughness, simple heat treatment process, small deformation, and both performance and process performance. It has been widely used in key components such as aircraft, ships, and missile shells. With the rapid development of aviation technology, the proportion of steel used in aircraft is gradually decreasing. Therefore, high-strength steel is required to achieve weight loss in the structure of flying parts. In recent years, the localization process of some (ultra) high-str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21J5/00B21J5/06C21D8/00C21D7/13
CPCB21J5/002B21J5/06C21D7/13C21D8/005
Inventor 梁艳唐军侯伟马鹏飞薛强
Owner SHAANXI HONGYUAN AVIATION FORGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap