A method for producing 5052h32 aluminum alloy plate in a short process

An aluminum alloy plate and short-process technology, applied in the field of alloy processing, can solve the problems of high cost, long cycle, and long production process, and achieve the effects of expanding temperature control, improving quality control, and saving energy

Active Publication Date: 2022-04-19
河南中孚高精铝材有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to propose a method for producing 5052H32 aluminum alloy plate with a short process to solve the problems of long production process, high cost and long cycle in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for producing 5052h32 aluminum alloy plate in a short process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention.

[0023] In describing the present invention, it should be understood that the terms "upper", "lower", "front", "rear", "left", "right", "top", "bottom", "inner", " The orientation or positional relationship indicated by "outside", etc. is based on the orientation or positional relationship shown in the drawings, and is only for the convenience of describing the present invention and simplifying the description, rather than indicating or implying that the referred device or element must have a specific orientation, so as to Specific orientation configurations and operations, therefore, are not to be construed as limitations on the invention.

[0024] see figure 1 , a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a short-flow method for producing 5052H32 aluminum alloy plates, belonging to the technical field of alloy processing. A method for producing 5052H32 aluminum alloy plates in a short process, comprising the following steps: S1, adjusting the formula, melting and casting aluminum slabs: adding 200-300ppm of Zr elements to the alloy formula, and performing aluminum slab melting and casting; S2, preheating: preheating The hot soaking temperature is controlled at 500°C; S3, hot rolling: use 1+4 hot tandem rolling mill to roll, and set the reduction amount, hot rough rolling pass, and hot rough rolling according to the thickness of the finished product during rolling. The thickness and temperature of the middle slab at the exit, the parking and maintenance temperature of the middle slab, the finish rolling exit temperature and the rolling speed; S4, air purging. The invention shortens the process flow and does not require cold rolling; during rolling, the characteristics of the hot rolling process are fully utilized, and the metal microstructure and mechanical property control in the quality requirements of the finished aluminum plate and strip are placed in the hot rolling process for coordinated control.

Description

technical field [0001] The invention relates to the technical field of alloy processing, in particular to a short-flow method for producing 5052H32 aluminum alloy plates. Background technique [0002] In recent years, my country's aluminum processing industry has developed rapidly, and many sets of hot rolling equipment have been introduced from abroad, such as Southwest Aluminum, Nanshan Aluminum, Chalco Ruimin, Henan Zhongfu, etc. These production lines have been put into operation one after another, which has a huge impact on the aluminum processing market at home and abroad. The growth rate of the aluminum plate consumption market is also getting faster and faster, especially the 5-series aluminum alloy plate, and the market demand for the 5052H32 state aluminum plate is strong. [0003] 5052 aluminum alloy belongs to the Al-Mg series heat treatment non-strengthenable aluminum alloy, in which the Mg content is 2.2-2.8%, and the Cr content is 0.15-0.35%. It has medium st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/08C22F1/047
CPCC22C21/08C22F1/047
Inventor 高振朋石磊纪欢欢韩昭勇王冬旭朱源源韩冰李栋李洁
Owner 河南中孚高精铝材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap