Method of eliminating iron scale from surface of stainless steel

A technology of stainless steel and iron scale, applied in the direction of abrasive feeding device, abrasive material, metal processing equipment, etc., can solve the problems of poor descaling effect, high consumption per ton of steel, affecting the surface quality of finished products, etc., and achieve the reduction of cleaning cost, The effect of reducing product cost

Inactive Publication Date: 2007-01-03
SHANXI TAIGANG STAINLESS STEEL CO LTD
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] During the hot rolling process of stainless steel cold-rolled raw materials, dense oxide scales are formed on the surface of the steel plate, which seriously affects the cleaning effect during the pickling process. Now the method of removing iron scale on the surface of stainless steel is the steel shot descaler method, which is easy to cause the surface of the raw material Oxide scale residues and increased roughness affect the surface quality of finished products. The effect of iron scale removal is poor. The surface roughness value of raw materials after pickling reaches 4μm or more, and the steel consumption per ton of steel shot is as high as 5Kg. Due to the quality of steel shot, At the same time, the iron scale on the surface of the raw material is not clean, and the steel shot dust is large, which increases the dust removal pressure and further affects the surface quality of the raw material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] The specific implementation of the present invention will be described below in conjunction with the examples, but the specific implementation of the present invention is not limited to the following examples.

[0011] What this embodiment removes is the 0Cr18Ni9 steel strip. In this embodiment, three shot blasting machines work successively and continuously remove the steel strip after the first one is removed by the second one, and finally by the third one.

[0012] Add SM150 steel grit to the silos of the three shot blasting machines, and use SM150 steel grit to remove iron scale on the surface of the stainless steel hot-rolled steel plate. The sand blasting coefficient is 1.1-1.2; The annealing temperature of the stainless steel hot-rolled steel plate should be 1130°C; the pressure current of the brush roller of the brushing machine in the pickling section after cleaning is 25A, the pressure of the cleaning water is 5-6Br, and the process speed of the stainless steel...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The elimination of iron scale on surface of stainless steel plate is completed with several shot blasting machines. The present invention features that SM150-type steel grits are filled into the material bin of the shot blasting machines and used in eliminating iron scale on surface of stainless steel plate. The present invention has sanding coefficient of 1.1-1.2, throwing head rotation speed of shot blasting machines of 1850-2000 rpm, annealing temperature of the hot rolled stainless steel plate of 1125-1140 deg.c, the brush roller pressure current in the pickling zone after elimination of 20-30 A, the washing water pressure not lower than 5Br and the technological speed of the hot rolled stainless steel plate of 60-67 m / min. Three shot blasting machines have separated thrown portions for high eliminating effect, and the present invention has low scale eliminating medium consumption, low cost and low surface roughness of the eliminated stainless steel plate.

Description

technical field [0001] The invention relates to a method for removing iron scale on the surface of stainless steel. Background technique [0002] During the hot rolling process of stainless steel cold-rolled raw materials, dense oxide scales are formed on the surface of the steel plate, which seriously affects the cleaning effect during the pickling process. Now the method of removing iron scale on the surface of stainless steel is the steel shot descaling method, which is easy to cause the surface of the raw material Residual scale and increased roughness will affect the surface quality of finished products, and the effect of removing iron scale is poor. The surface roughness value of raw materials after pickling can reach more than 4μm, and the consumption per ton of steel shot is as high as 5Kg. Due to the quality of steel shot, At the same time, the iron scale on the surface of the raw material is not clean, and the steel shot dust is large, which increases the dust remo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B24C1/04B24C7/00
Inventor 穆景权李旭初
Owner SHANXI TAIGANG STAINLESS STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products