A fabric elastic floor and its processing method

Abstract

The invention discloses a cloth elastic floor and a machining method of the cloth elastic floor, and belongs to the field of building floor materials. The cloth elastic floor has no pollution, and is environmentally friendly, durable, abrasion-resistant, elastic, good in foot feeling and diverse in style, and the thermal expansion and cold contraction of the floor can be effectively controlled. The cloth elastic floor comprises a bottom material layer, a lower-layer EVA film layer is arranged above the bottom material layer, a cloth layer is arranged above the lower-layer EVA film layer, an upper-layer EVA film layer is arranged above the cloth layer, an abrasion-resistant layer is arranged above the upper-layer EVA film layer, and the bottom material layer, the cloth layer and the abrasion-resistant layer are compounded through the upper-layer EVA film layer and the lower-layer EVA film layer in a vacuum heat compounding mode. The invention further discloses the machining method of the cloth elastic floor. The machining method resolves the problem of bubbles and avoids the situation that products are not flat. The cloth elastic floor and the machining method of the cloth elastic floor are suitable for installation of building floors.

Description

technical field

[0001] The present invention relates to a kind of building floor material, more specifically, it relates to a kind of fabric elastic floor, and the present invention also relates to the processing method of above-mentioned floor. Background technique

[0002] At present, the elastic floor is mainly PVC floor. The buffer layer of this kind of floor is a PVC layer, but the PVC layer is relatively hard, resulting in poor foot feel of the PVC floor. Nevertheless, the popularity rate of EVA flooring is still far inferior to that of PVC flooring. The main reasons are: (1) During the processing of EVA flooring, a large number of air bubbles enter the EVA film layer and cause the floor to be uneven. This is the current technology of EVA fabric elastic flooring. Difficulties; (2) The EVA floor has the phenomenon of thermal expansion and contraction; (3) The color layer pattern of the EVA floor is single. Contents of the invention

[0003] The object of the present ...

Examples

Embodiment 1

[0028] refer to figure 1 As shown, the present invention provides a kind of cloth art elastic floor, the top of described primer layer 1 is lower floor EVA film layer 2, the top of described lower floor EVA film layer 2 is cloth layer 3, the top of described cloth layer 3 is upper floor EVA Film layer 4, above the upper layer of EVA film layer 4 is a wear-resistant layer 5, and the bottom material layer 1, cloth layer 3 and wear-resistant layer 5 form a whole by vacuum thermal compounding of the upper and lower layers of EVA film layers; The total thickness of the fabric elastic floor is 6 mm, and the base material layer 1 is made of wood-plastic composite material with a thickness of 2 mm. The lower EVA film layer 2 and the upper EVA film layer 4 are ethylene-vinyl acetate copolymers, and the sum of the thicknesses of the lower EVA film layer 2 and the upper EVA film layer 4 is 2 mm. The cloth layer 3 adopts non-woven fabric, and the thickness of the cloth layer 3 is 1.9mm. ...

Embodiment 2

[0030] refer to figure 1 , the present invention provides a fabric elastic floor. The total thickness of the fabric elastic floor in this embodiment is 8mm. . The sum of the thicknesses of the lower EVA film layer 2 and the upper EVA film layer 4 is 3mm. The cloth layer 3 adopts calico, and the thickness of the cloth layer 3 is 1.8mm. The wear-resistant layer 5 adopts polyvinyl chloride with a thickness of 0.2.

Embodiment 3

[0032] refer to figure 1 , the present invention provides a kind of cloth art elastic floor, the total thickness of the cloth art elastic floor of this embodiment is 10mm, this embodiment is basically the same as embodiment 1, the different place is that the base material layer 1 of this embodiment adopts the polystyrene layer with a thickness of 4mm. vinyl chloride. The sum of the thicknesses of the lower EVA film layer 2 and the upper EVA film layer 4 is 4mm. The cloth layer 3 adopts woven cloth, and the thickness of the cloth layer 3 is 1.7mm. The wear-resistant layer 5 adopts polyurethane with a thickness of 0.3.

technical field

[0001] The present invention relates to a kind of building floor material, more specifically, it relates to a kind of fabric elastic floor, and the present invention also relates to the processing method of above-mentioned floor. Background technique

[0002] At present, the elastic floor is mainly PVC floor. The buffer layer of this kind of floor is a PVC layer, but the PVC layer is relatively hard, resulting in poor foot feel of the PVC floor. Nevertheless, the popularity rate of EVA flooring is still far inferior to that of PVC flooring. The main reasons are: (1) During the processing of EVA flooring, a large number of air bubbles enter the EVA film layer and cause the floor to be uneven. This is the current technology of EVA fabric elastic flooring. Difficulties; (2) The EVA floor has the phenomenon of thermal expansion and contraction; (3) The color layer pattern of the EVA floor is single. Contents of the invention

[0003] The object of the present ...

Examples

Embodiment 1

[0028] refer to figure 1 As shown, the present invention provides a kind of cloth art elastic floor, the top of described primer layer 1 is lower floor EVA film layer 2, the top of described lower floor EVA film layer 2 is cloth layer 3, the top of described cloth layer 3 is upper floor EVA Film layer 4, above the upper layer of EVA film layer 4 is a wear-resistant layer 5, and the bottom material layer 1, cloth layer 3 and wear-resistant layer 5 form a whole by vacuum thermal compounding of the upper and lower layers of EVA film layers; The total thickness of the fabric elastic floor is 6 mm, and the base material layer 1 is made of wood-plastic composite material with a thickness of 2 mm. The lower EVA film layer 2 and the upper EVA film layer 4 are ethylene-vinyl acetate copolymers, and the sum of the thicknesses of the lower EVA film layer 2 and the upper EVA film layer 4 is 2 mm. The cloth layer 3 adopts non-woven fabric, and the thickness of the cloth layer 3 is 1.9mm. ...

Embodiment 2

[0030] refer to figure 1 , the present invention provides a fabric elastic floor. The total thickness of the fabric elastic floor in this embodiment is 8mm. . The sum of the thicknesses of the lower EVA film layer 2 and the upper EVA film layer 4 is 3mm. The cloth layer 3 adopts calico, and the thickness of the cloth layer 3 is 1.8mm. The wear-resistant layer 5 adopts polyvinyl chloride with a thickness of 0.2.

Embodiment 3

[0032] refer to figure 1 , the present invention provides a kind of cloth art elastic floor, the total thickness of the cloth art elastic floor of this embodiment is 10mm, this embodiment is basically the same as embodiment 1, the different place is that the base material layer 1 of this embodiment adopts the polystyrene layer with a thickness of 4mm. vinyl chloride. The sum of the thicknesses of the lower EVA film layer 2 and the upper EVA film layer 4 is 4mm. The cloth layer 3 adopts woven cloth, and the thickness of the cloth layer 3 is 1.7mm. The wear-resistant layer 5 adopts polyurethane with a thickness of 0.3.