Preparation method of a three-dimensional graphene/silver nanoflower stretchable biosensor material

A biosensor and graphene technology, applied in biological testing, material inspection products, etc., can solve the problems of insufficient tensile stability, low physical enhancement, and low sensitivity, and achieve low defect peaks, high chemical adsorption, and high crystallinity quality effect

CN106546720BActive Publication Date: 2020-05-05SHANDONG NORMAL UNIV
12 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
Publication Date
2020-05-05

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention discloses a preparation method of a three dimensional graphene / silver nanoflower stretchable biosensor material. The method comprises the following steps: (1) three dimensional graphene is prepared on a foam metal substrate, in order to obtain a graphene / foam metal composite material; (2) the graphene / foam metal composite material is immersed in an etching solution, after the foam metal substrate is dissolved, a stamping method is used for fishing the three dimensional graphene material out from the etching solution; (3) the elastic substrate is prestretched at a direction or orthotropically stretched at two directions, the substrate is recovered to an original state slowly, and a stretchable three dimensional graphene structure is obtained; (4) silver nanoflowers are grown on the elastic substrate of the stretchable graphene structure obtained in the step (3).
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a preparation method of a stretchable biosensor material, in particular to a preparation method and application of a three-dimensional graphene / silver nanoflower stretchable biosensor material, and belongs to the technical field of new materials. Background technique

[0002] For today's biosensors, high sensitivity, high stability, and high efficiency are crucial. The highly sensitive in situ SERS technology can detect environmental and agricultural product pollution and the canceration caused by it in real time and quickly, which plays an important role in pollution control and medical diagnosis and treatment. At present, the progress of related research is relatively slow, mainly because it is difficult to prepare highly sensitive stretchable materials.

[0003] The research on stretchable biosensors plays an important role in environmental monitoring, pollution control, medical diagnosis and treatment, etc., and has become...

Examples

Embodiment 1

[0050] Graphene is grown on the three-dimensional substrate nickel foam to obtain a graphene / nickel particle hybrid structure, and finally a graphene / silver nanoflower hybrid structure, such as figure 1 The preparation roadmap includes the following preparation steps:

[0051] 1. Take nickel foam with a size of 8cm×8cm and place it in a tube furnace;

[0052] 2. Turn on the vacuum pump to pump the air pressure of the tube furnace to the ultimate vacuum state of 3×10 -6 Torr;

[0053] 3. Keep vacuum 3×10 -6 After Torr for 15 minutes (the effect of vacuum for 15 minutes is to remove impurities, air, etc. inside the quartz tube to ensure that the reaction chamber is clean), the air pressure of the quartz tube 3 is raised to 3 × 10 -3 Torr;

[0054] 4. Set the hydrogen flow meter to 100sccm, and inject hydrogen into the vacuum chamber;

[0055] 5. After the tube furnace temperature rises to 300°C, anneal at a constant temperature for 20 minutes;

[0056] 6. After the tube f...

Embodiment 2

[0078] Graphene is grown on the three-dimensional substrate copper foam to obtain a graphene / copper foam hybrid structure, and finally a graphene / silver nanoflower hybrid structure is obtained, such as figure 1 The preparation roadmap includes the following preparation steps:

[0079] 1. Take foam copper with a size of 8cm×8cm and place it in a tube furnace;

[0080] 2. Turn on the vacuum pump to pump the air pressure of the tube furnace to the limit vacuum state of 3×10 -6 Torr;

[0081] 3. Keep the vacuum state 3×10 -6 After Torr for 15 minutes (the effect of vacuum for 15 minutes is to remove impurities, air, etc. inside the quartz tube to ensure that the reaction chamber is clean), the air pressure of the quartz tube 3 is raised to 3 × 10 -3 Torr;

[0082] 4. Set the hydrogen flow meter to 100 sccm, inject hydrogen into the vacuum chamber;

[0083] 5. After the tube furnace temperature rises to 300°C, anneal at a constant temperature for 20 minutes;

[0084] 6. Afte...