Preparation method of a stretchable supercapacitor based on a highly conductive graphene/nickel particle hybrid structure

A technology of supercapacitors and hybrid structures, applied in the field of capacitors, can solve the problems of complex preparation process of stretchable graphene-based active materials, inability to directly apply stretchable supercapacitors, and affecting the performance of stretchable supercapacitors. Low peak, good conductivity, simple and controllable effect

CN104882297BInactive Publication Date: 2017-05-24SHANDONG NORMAL UNIV
4 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
Publication Date
2017-05-24
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention relates to a preparation method of a stretchable supercapacitor based on a highly conductive graphene / nickel particle hybrid structure. First, a sponge-like graphene material is prepared on foamed nickel by chemical vapor deposition, and the prepared graphene / nickel foam is prepared Immersed in the etching solution, react slowly, so that most of the nickel metal is chemically replaced, so that the nickel metal is transformed into small nickel particles, and then the sponge-like graphene / nickel particle mixed structure is removed from the engraved The pre-stretched elastic substrate slowly returns to the original length or area, and the prepared stretchable graphene / nickel particle hybrid structure is used as the electrode material, according to the elastomer / electrode / The structure of solid electrolyte / electrode / elastomer to prepare all-solid-state stretchable supercapacitors. The invention increases the capacitance of the traditional capacitor, reduces the contact resistance, has good tensile stability, many times, excellent performance, low cost, controllable method and is suitable for mass production.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a preparation method of a stretchable capacitor, in particular to a preparation method of a stretchable supercapacitor with a highly conductive sponge-like graphene / nickel particle mixed nanostructure, belonging to the technical field of capacitors. Background technique

[0002] As a new type of electronic equipment today, stretchable electronic devices can still exhibit good electrical properties under the condition of large mechanical stress, and have a wide range of applications in human implants, flexible portable devices, wearable devices, wireless sensing devices, etc. the use of. To realize its independent driving ability, it is particularly important to develop stretchable energy storage devices such as supercapacitors. However, the progress of related research is relatively slow, mainly because it is difficult to prepare stretchable electrode materials with excellent electrical and electrochemical properties. [0003...

Examples

Embodiment 1

[0051] 1. Take nickel foam with a size of 8cm×8cm and place it in a tube furnace;

[0052] 2. Turn on the vacuum pump to pump the air pressure of the tube furnace to the ultimate vacuum state of 3×10 -6 Torr;

[0053] 3. Keep vacuum 3×10 -6 After Torr for 15 minutes (the effect of vacuum for 15 minutes is to remove impurities, air, etc. inside the quartz tube to ensure that the reaction chamber is clean), the air pressure of the quartz tube 3 is raised to 3 × 10 -3 Torr;

[0054] 4. Set the hydrogen flow meter to 100sccm, and inject hydrogen into the vacuum chamber;

[0055] 5. After the tube furnace temperature rises to 300°C, anneal at a constant temperature for 20 minutes;

[0056] 6. After the tube furnace temperature rises to 1000°C, inject methane into the vacuum chamber, set the gas flow meter to 200 sccm, and stay for 30 minutes for growth;

[0057] 7. Turn off the methane gas flow meter and quickly lower the temperature of the tube furnace to room temperature at ...

Embodiment 2

[0079] Graphene is grown on a nickel foam substrate and finally a graphene / nickel particle hybrid structure is grown to prepare a stretchable capacitor, including the following preparation steps

[0080] 1. Take nickel foam with a size of 8cm×9cm and place it in a tube furnace;

[0081] 2. Turn on the vacuum pump to pump the air pressure of the tube furnace to the ultimate vacuum state of 3×10 -6 Torr;

[0082] 3. Keep vacuum 3×10 -6 After Torr for 15 minutes (the effect of vacuum for 15 minutes is to remove impurities, air, etc. inside the quartz tube to ensure that the reaction chamber is clean), the air pressure of the quartz tube 3 is raised to 3 × 10 -3 Torr;

[0083] 4. Set the hydrogen flow meter to 100sccm, and inject hydrogen into the vacuum chamber;

[0084] 5. After the tube furnace temperature rises to 300°C, anneal at a constant temperature for 20 minutes;

[0085] 6. After the tube furnace temperature rises to 1000°C, inject methane into the vacuum chamber, ...

Embodiment 3

[0110] Graphene is grown on a nickel foam substrate and finally a graphene / nickel particle hybrid structure is grown to prepare a highly conductive stretchable capacitor, including the following preparation steps:

[0111]1. Take nickel foam with a size of 5cm×9cm and place it in a tube furnace;

[0112] 2. Turn on the vacuum pump to pump the air pressure of the tube furnace to the ultimate vacuum state of 3×10 -6 Torr;

[0113] 3. Keep vacuum 3×10 -6 After Torr for 15 minutes (the effect of vacuum for 15 minutes is to remove impurities, air, etc. inside the quartz tube to ensure that the reaction chamber is clean), the air pressure of the quartz tube 3 is raised to 3 × 10 -3 Torr;

[0114] 4. Set the hydrogen flow meter to 100sccm, and inject hydrogen into the vacuum chamber;

[0115] 5. After the tube furnace temperature rises to 300°C, anneal at a constant temperature for 20 minutes;

[0116] 6. After the tube furnace temperature rises to 1000°C, inject methane into th...