Method for improving hot processing performance of TiAl alloy

A thermal processing and alloying technology, which is applied in the direction of manufacturing tools and other manufacturing equipment/tools, etc., can solve the problems of poor high-temperature thermal processing performance, high production cost, and narrow thermal processing window of TiAl alloy, so as to improve thermal processing performance and thermal processing performance. Wide processing window and good thermal processing performance at high temperature

Inactive Publication Date: 2010-09-01
HARBIN INST OF TECH
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to solve the problems of high production cost, poor high-temperature thermal processing performance and narrow thermal processing window of the existing methods for improving the thermal processing performance of TiAl alloys, and provides a method for improving the thermal processing performance of TiAl alloys. method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving hot processing performance of TiAl alloy
  • Method for improving hot processing performance of TiAl alloy
  • Method for improving hot processing performance of TiAl alloy

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0016] Specific embodiment one: the method for improving the hot workability of TiAl alloy in this embodiment is carried out according to the following steps:

[0017] 1. Melting: first add Mo element to TiAl alloy, and then use water-cooled copper crucible induction melting method to produce TiAl alloy ingot;

[0018] 2. Hot isostatic pressing: heat-preserve the TiAl alloy ingot at a temperature of 1250-1280°C and a pressure of 130-140Mpa for 4-5 hours, then cool it with the furnace and take it out of the furnace;

[0019] 3. Homogenization annealing: the TiAl alloy ingot obtained after hot isostatic pressing is heat-preserved at a temperature of 1250-1300°C for 12-24 hours, then cooled with the furnace and taken out of the furnace;

[0020] 4. Wire electric discharge cutting: cutting the TiAl alloy ingot obtained after homogenizing annealing into cylindrical ingots;

[0021] 5. Wrapping sealing welding: Spray the glass lubricant with a thickness of 0.1-0.15mm on the surface...

specific Embodiment approach 2

[0026] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is that in step 2, the temperature is 1270° C. and the pressure is 135 Mpa, and the heat preservation treatment is carried out for 4.5 hours. Other steps and parameters are the same as those in Embodiment 1.

specific Embodiment approach 3

[0027] Specific embodiment 3: This embodiment differs from specific embodiments 1 to 2 in that: in step 3, heat preservation treatment is carried out at a temperature of 1270° C. for 16 hours. Other steps and parameters are the same as those in Embodiments 1 to 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for improving hot processing performance of TiAl alloy, which relates to a method for improving the hot processing performance of alloy and solves the problems that the conventional method for improving the hot processing performance of the TiAl alloy has high manufacturing cost and the manufactured TiAl alloy has poor high-temperature hot processing performance and narrow hot processing window. The method comprises the following steps of: 1, smelting; 2, hot isostatic pressing; 3, homogenizing annealing; 4, electro-spark wire cutting; 5, sheathing and sealing; 6, heat preservation and hot extrusion to improve the hot processing performance of the TiAl alloy. The TiAl alloy manufactured by the method has wide hot processing window and good high-temperature hot processing performance; and compared with the conventional multi-step hot mechanical processing method for improving the hot processing performance of the TiAl alloy, the manufacturing method of the invention reduces the cost by over 50 percent.

Description

technical field [0001] The invention relates to a method for improving the thermal processing performance of an alloy. Background technique [0002] The research and application of high-temperature structural materials is an important factor for the revolutionary change and development of aerospace propulsion systems in the 21st century. Due to its excellent high-temperature performance, TiAl intermetallic compound has become a new type of lightweight high-temperature structural material that has been widely concerned and rapidly developed at home and abroad, and has entered the stage of practical research. The NASA report pointed out that by 2020, the amount of TiAl-based alloys and their composite materials will account for about 20% of aerospace engines. [0003] By controlling and optimizing the microstructure of TiAl-based alloys, an alloy with a fine-grained full-lamellar structure can be obtained, which can basically solve the defect that the tensile strength, plasti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P23/04
Inventor 单德彬徐文臣张浩柏杨吕炎
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap