Three-component fiber blended yarns and manufacturing process thereof

A technology of fiber blending and manufacturing process, which is applied in textiles, papermaking, yarn and other directions to achieve accurate fiber content and solve sticking effects

Active Publication Date: 2010-11-24
JIHUA 3542 TEXTILE CO LTD
View PDF1 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to meet the current market demand for the continuous pursuit of functionality of textile fabrics, uniformly mix raw materials with different physical properties and different functions according to the speci

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Three-component fiber blended yarns and manufacturing process thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] The specific implementation of the present invention will be further described in detail below in conjunction with examples:

[0017] Because the vinylon fiber is thicker than the polyester fiber, according to the fiber characteristics, the vinylon fiber transfers outwards in the yarn, which plays a role in improving the wear resistance. The choice of 20% high-strength vinylon can meet the requirements of wear resistance for clothing. Choose 20% The purpose of grade 3 fine-staple cotton is to meet the functional requirements of human comfort.

[0018] Example 1: 60% ordinary polyester fiber, 20% vinylon fiber and 20% fine lint cotton, polyester fiber selects 1.33dtex*38mm, vinylon fiber selects high-strength type, specification 1.65dtex*38mm.

[0019] The three-component fiber blended spinning process steps are:

[0020] 1. Blowing process: Because the fine-staple cotton contains impurity and short-staple, it also needs to go through a combing process, so the fine-staple cotton...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses three-component fiber blended yarns, which are characterized by comprising 60 to 70 percent of polyester fiber, 15 to 25 percent of vinylon fiber, 15 to 25 percent of upland cotton fiber, wherein the warp and weft count in the yarns is 19.6*2. A manufacturing process of the three-component fiber blended yarns comprises the following steps of: cotton clearing, cotton carding, pre-drawing, combing, drawing, roving and spinning to complete the spinning of the three-component fiber blended yarns. The three-component fiber blended yarns have accurate fiber content and can solve the problem of sticky winding during spinning. Products manufactured by the process can be made into blended fabrics of the polyester fiber, the vinylon fiber and the cotton fiber, so wear-resisting and comfortable blended products are provided for the field of spinning.

Description

technical field [0001] The invention relates to the control of the blending ratio of a multi-component fiber-mixed spinning product, in particular to a blended spinning of polyester fiber, vinylon fiber and fine-staple cotton fiber and its manufacturing process. Background technique [0002] At present, new fibers in the textile industry are constantly being developed, breaking the original traditional combination of pure cotton spinning or polyester-cotton blended yarns, and replacing them with a variety of functional fibers to form fashion or professional wear with different styles. In addition to requirements for shape retention, wrinkle resistance, pilling resistance, good drape, bright colors, color fastness, and good gloss in clothing textiles and home textiles, people also put forward new key popular uses for new functional fibers, such as comfort It is required to be warm, cool, moisture-absorbing, sweat-conducting, quick-drying, soft, and non-itchy; in terms of safe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D02G3/04
Inventor 邱卫兵张慧霞张纯芳刘定会刘辉
Owner JIHUA 3542 TEXTILE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap