A setting method, ferrite technology, applied in the field of metallurgy, can solve problems such as unstable slab width

Inactive Publication Date: 2013-02-13
BAOSHAN IRON & STEEL CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] It is based on this that the control of slab width is very unstable in the current production process of ferritic stainless steel plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for setting width of ferrite stainless steel slab during continuous casting production
  • Method for setting width of ferrite stainless steel slab during continuous casting production
  • Method for setting width of ferrite stainless steel slab during continuous casting production

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] In this embodiment, ferritic stainless steel SUS410S is selected, and the target width of the slab is W Cold is 1265mm, then to obtain a ferritic stainless steel slab that meets the requirements, proceed through the following steps:

[0056] (1) Calculate the shrinkage rate in the width direction of the ferritic stainless steel SUS410S slab from the temperature at the outlet of the continuous casting machine crystallizer to the temperature when it is cooled to room temperature

[0057] W T = W Mold ∫ T cold T M - ex α ( T ) dT - - - ( 1.1 )

[0058] The thermal expansion coefficient α(T)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for setting the width of a ferritic stainless steel slab in continuous casting production. The temperature when the temperature is cooled to room temperature, the shrinkage rate in the width direction; calculate the expansion value of the steel slab in the width direction from the beginning of creep to the end of creep; according to the expansion value of the steel slab Target width, adjust the position of the copper plates on both sides of the mold of the continuous casting machine, so as to set the width of the mold outlet. The method conforms to the performance characteristics of ferritic steel grades, and in terms of control results, it can produce slabs that meet the preset product requirements, and at the same time meet the requirements of small errors and stable control laws.

Description

technical field [0001] The invention relates to the field of metallurgy, in particular to a size control method in the steel plate casting process. Background technique [0002] Continuous casting technology is a process in which molten steel is poured, condensed, and cut to obtain a slab. Such as figure 1 As shown, the most important part of this process is to pour one or more furnaces of molten steel into the crystallizer 3 continuously through the ladle 1 and the tundish 2, and then water-cool in the crystallizer 3 composed of four copper plates to obtain a solid shell around , The middle part is still the slab of molten steel. Then the cast slab is gradually solidified through the secondary cooling 4, and is pulled out of the continuous casting machine body by the support and rotation of the rollers in the tension straightening device 5, and then cut into slabs of a certain length by the cutting device. [0003] In continuous casting production, the width of the produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/16
Inventor 苏锦盛建华陆力军刘文彬
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap