A cross-linked polyethylene, DC cable technology, applied in the direction of conductor/cable insulation, insulator, circuit, etc., can solve the problem of different breakdown strength, achieve the effect of meeting electrical performance requirements, reliable transmission, and ensuring long-term stable operation

Active Publication Date: 2013-01-02
XI AN JIAOTONG UNIV +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0030] 2) The breakdown strength is different
Under the action of DC voltage, the problem of partial discharge is relatively less serious
[0032] Therefore, the structural dimensions of XLPE insulated DC cables are completely different from those of AC cables, and the structural dimensions of AC cables cannot be copied for DC cables.
Also, the insulation design method for AC cables is not applicable to DC cables

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Design method for insulation thickness of high-voltage cross-linked polyethylene direct current (DC) cable
  • Design method for insulation thickness of high-voltage cross-linked polyethylene direct current (DC) cable
  • Design method for insulation thickness of high-voltage cross-linked polyethylene direct current (DC) cable

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0072] The present invention will be described in more detail below in combination with specific embodiments.

[0073] Using the insulation thickness design method proposed by the present invention to design the insulation thickness of the 110kV single-core XLPE DC cable includes the following steps:

[0074] Step 1: Determine the form of the design voltage. When designing the insulation thickness of the high-voltage XLPE DC cable, the designed voltage form is the DC voltage U dc , Polarity reversal voltage U fz and DC voltage superimposed on the transient overvoltage U pu ;

[0075] Step 2: Calculate the magnitude of the design voltage, DC voltage U dc The long-term rated operating voltage U of 110kV single-core XLPE DC cable 0 , is 110kV, namely U dc =U 0 =110kV, polarity reversal voltage U fz The value is 1.45U 0 , namely U fz =1.45U 0 =160kV, while the transient overvoltage U is superimposed on the DC voltage pu The value is (1.1K+1.9)U 0 , namely U pu =(1.1K+...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a design method for insulation thickness of a high-voltage cross-linked polyethylene direct current (DC) cable. The design method comprises the following steps of: determining the form of design voltage; calculating the amplitude of the design voltage; determining the form of design field intensity corresponding to the form of the voltage design; testing and calculating the amplitude of the design field intensity; and calculating and determining the design thickness of the high-voltage cross-linked polyethylene DC cable. For the high-voltage cross-linked polyethylene DC cable product designed by the design method for the insulation thickness, the cross-linked polyethylene insulation can withstand the action of long-term operating voltage of DC power transmission lines, power frequency alternating current (AC) voltage superimposed on the DC, voltage in a system, polarity inverse voltage produced through current reversal, operation impulse voltage produced through on / off actions and lightning impulse atmospheric over voltage, meets the requirements on electrical properties of cable insulation, ensures the long-term stable operation of the cable and realizes the reliable transmission of electric energy.

Description

technical field [0001] The invention relates to a method for designing the insulation thickness of a cable, in particular to a method for designing the insulation thickness of a high-voltage cross-linked polyethylene direct current cable. Background technique [0002] The insulation thickness design methods of high-voltage AC cables include: [0003] 1) Maximum field strength method [0004] In the cable insulation layer, the maximum field strength appears on the surface of the wire core. If the breakdown strength of the insulating material is greater than the maximum field strength, the insulation thickness can be calculated using the maximum field strength formula. The calculation formula is: [0005] E ∞ m = U r c ln R r c ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): H01B13/06H01B19/00
Inventor刘英曹晓珑钟力生赵文明吴丽芳朱华英
OwnerXI AN JIAOTONG UNIV