Interior wall paint glazing agent capable of generating glittering effect

Abstract

The invention discloses an interior wall paint glazing agent capable of generating glittering effect. The glazing agent uses polyacrylate dispersion as a film-forming substance and is prepared by adding large particle size mica slice as a functional filling material, silica delustering agent as a functional auxiliary agent, polyvinyl alcohol aqueous solution with low degree of polymerization as a levelling agent and dispersing agent into a common glazing agent containing film forming auxiliary agent, mildew inhibitor, antifoaming agent, antifreezing agent and water, etc. A formula of the glazing agent comprises (wt%) 15.0-40.0 parts of water, 25.0-60.0 parts of polyacrylate emulsion, 1.0-2.5 parts of powdered mica slice, 0.2-1.5 parts of delustering agent, 8.0-20.0 parts of polyving akohol aqueous solution, 1.0-2.5 parts of film-forming auxiliary agent, 0.05-0.2 part of mildew inhibitor, 0.05-0.2 part of antifoaming agent and 0.5-1.6 parts of antifreezing agent.

Description

Technical field:

[0001] The invention relates to a varnishing agent for interior wall coatings. Due to the addition of powdery mica flakes with coarse particle diameters in the varnishing agent, and the amount of the addition is controlled, the coating film has the effect of light flickering under light irradiation. Improve the decorative performance of the coating film. At the same time, a matting agent and a leveling agent are added to meet the required functional requirements. At the same time, the stain resistance and scrub resistance of the coating film are improved, so that the coating film can be easily cleaned after being stained. Background technique:

[0002] The usual thin interior wall paints are monotonous and dull in decoration, so in some special parts, other types of decorative materials or higher performance paints have to be used instead; due to the poor leveling of water-based paints (such as latex paints), the Its coating film is rough, more likely to be...

Examples

Example Embodiment

[0012] Example

[0013] (1) The formula (mass%) is: water 25.0~30.0; polyacrylate emulsion 35.0~40.0, powdered mica flake 1.5~2.0, matting agent 0.7~1.2, polyvinyl alcohol aqueous solution 15.0~20.0, film forming aid 1.5 ~2.0; Anti-mold agent 0.1~0.15; Antifoaming agent 0.1~0.15; Antifreeze agent 1.0~1.3.

[0014] (2) The preparation method is: in a container that can produce high-speed stirring, inject water, antifungal agent, antifreeze and defoamer according to the formula, and stir and disperse evenly; add silica matting agent and stir at high speed to make it fully dispersed And then put the powdered mica flakes into high-speed stirring to make it fully dispersed; finally put into the polyacrylate emulsion and stir evenly to obtain the polishing agent of the present invention.

Technical field:

[0001] The invention relates to a varnishing agent for interior wall coatings. Due to the addition of powdery mica flakes with coarse particle diameters in the varnishing agent, and the amount of the addition is controlled, the coating film has the effect of light flickering under light irradiation. Improve the decorative performance of the coating film. At the same time, a matting agent and a leveling agent are added to meet the required functional requirements. At the same time, the stain resistance and scrub resistance of the coating film are improved, so that the coating film can be easily cleaned after being stained. Background technique:

[0002] The usual thin interior wall paints are monotonous and dull in decoration, so in some special parts, other types of decorative materials or higher performance paints have to be used instead; due to the poor leveling of water-based paints (such as latex paints), the Its coating film is rough, more likely to be...

Examples

Example Embodiment

[0012] Example

[0013] (1) The formula (mass%) is: water 25.0~30.0; polyacrylate emulsion 35.0~40.0, powdered mica flake 1.5~2.0, matting agent 0.7~1.2, polyvinyl alcohol aqueous solution 15.0~20.0, film forming aid 1.5 ~2.0; Anti-mold agent 0.1~0.15; Antifoaming agent 0.1~0.15; Antifreeze agent 1.0~1.3.

[0014] (2) The preparation method is: in a container that can produce high-speed stirring, inject water, antifungal agent, antifreeze and defoamer according to the formula, and stir and disperse evenly; add silica matting agent and stir at high speed to make it fully dispersed And then put the powdered mica flakes into high-speed stirring to make it fully dispersed; finally put into the polyacrylate emulsion and stir evenly to obtain the polishing agent of the present invention.