Production process of nano titanium pearl fiber anti-electromagnetic textile yarns

A technology of pearl fiber and textile yarn, which is applied in fiber processing, textiles and papermaking, etc., can solve the problem that pearl fiber does not have anti-radiation function, and achieve the effect of reducing damage and reducing the chance of cancer

Inactive Publication Date: 2012-07-04
XIAN ZONGHENG TEXTILE TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to propose a production process of nano-titanium pearl fiber anti-electromagnetic textile yarn, which solves the problem that the commonly used pearl fiber does not have a radiation protection function, further increases the usage of pearl fiber, and wider application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 1. Preparation of padding liquid: the content and dosage of the padding liquid are titanium powder (30-60nm) 30g / L, penetrating agent JFC2ml / L, fixing agent WLS20g / L, binder BH15g / L, NaOH3g / L . Among them, the adhesive and fixing agent are added first, and the titanium powder is added after stirring evenly;

[0017] 2. Padding: Two dipping and two rolling methods, roll speed: 2r / min, roll pressure: 0.08Mpa;

[0018] 3. Drying: Dry at 100°C for 12 minutes;

[0019] 4. Baking: Baking at 130°C for 4 minutes.

Embodiment 2

[0021] 1. Preparation of padding liquid: the content and dosage of the padding liquid are titanium powder (30-60nm) 35g / L, penetrating agent JFC3ml / L, fixing agent WLS25g / L, binder BH20g / L, NaOH4g / L . Adding order is with embodiment one;

[0022] 2. Padding: Two dipping and two rolling methods are adopted, roll speed: 2.5r / min, roll pressure: 0.1Mpa;

[0023] 3. Drying: Dry at 105°C for 10 minutes;

[0024] 4. Baking: Baking at 140°C for 3 minutes.

Embodiment 3

[0026] 1. Preparation of padding liquid: the substances and dosages contained in the padding liquid are titanium powder (30-60nm) 40g / L, penetrating agent JFC5ml / L, fixative WLS30g / L, adhesive BH25g / L, NaOH5g / L . Adding order is with embodiment one;

[0027] 2. Two dipping and two rolling methods are adopted, roll speed: 3r / min, roll pressure: 0.12Mpa;

[0028] 3. Drying: Dry at 110°C for about 8 minutes;

[0029] 4. Baking: Baking at 150°C for 2 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a production process of nano titanium pearl fiber anti-electromagnetic textile yarns. In the production of the titanium pearl fiber anti-electromagnetic textile yarns, a padding liquid with optimal components and optimal concentration is prepared by using nano titanium powder and artificially synthesized fixative WLS, the padding liquid is applied on the pearl fiber by adopting a double-dip-double-nip manner, and the fixation effect of the titanium powder on the pearl fiber is enhanced by adopting an optimal baking process. The produced titanium pearl fiber radiation-resistant composite yarns have the titanium powder content more than 30%; the product produced from the yarns has a good radiation protection effect; and the product prepared from the radiation-resistant composite titanium pearl fiber produced by the production process satisfies the radiation protection requirement of people.

Description

technical field [0001] The invention relates to a production process of nano-titanium pearl fiber anti-electromagnetic textile yarn. The compounded titanium pearl fiber has good radiation-proof function. Background technique [0002] In the information age, electromagnetic radiation is an "invisible killer" that people often neglect to prevent. Power plants, broadcasting, TV communication transmission systems, mobile phones, and household appliances are all electromagnetic radiation sources. Relevant experts believe that finance, radio and television, IT, electric power Eight industries, including telecommunications, civil aviation, railway, and medical care, are high-risk industries that are prone to electromagnetic radiation pollution. In addition, the electromagnetic radiation of various electrical appliances in the living environment is not easy to ignore. Among them, the electromagnetic radiation of microwave ovens, computers and mobile phones has reached 200 milligauss...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/83
Inventor 李小龙
Owner XIAN ZONGHENG TEXTILE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com