Preparation method of novel matte anti-static release paper

An anti-static, release paper technology, used in paper, papermaking, paper coatings, etc., can solve the problems of low bonding force between the coating layer and the release agent coating, unstable peeling force, etc. Surface anti-static performance, improve anti-static effect, improve scratch resistance effect

Active Publication Date: 2015-07-22
JIANGSU SIDIKE NEW MATERIALS SCI & TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the invention is to provide a preparation method of a novel matte antistatic release paper, which not only solves the binding force of the coating layer of the release paper and the release agent coating Not high, unstable peeling force, but also improves the anti-static performance of the film surface, and also improves the scratch resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of novel matte anti-static release paper
  • Preparation method of novel matte anti-static release paper
  • Preparation method of novel matte anti-static release paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1~5

[0028] Embodiment 1~5: a kind of preparation method of novel matte surface antistatic release paper mainly consists of the following steps:

[0029] Step 1. Use a laminating machine to coat a film layer 2 on one surface of a release paper base paper 1. After the film layer 2 is cooled, apply an adhesive layer on the other surface of the release paper base paper 1 3 to obtain the substrate layer;

[0030] Step 2, coating a layer of matte antistatic coating 5 with a thickness of 0.2 to 2 microns on one surface of a film layer 4, the matte antistatic coating 5 is composed of the following components in mass percentage:

[0031] Silica particles 2~6%,

[0032] Acrylic polyols with an average molecular weight of 500~2000 20~30%,

[0033] Polyoxyalkylene series polyol resin with an average molecular weight of 200~2500 35~45%,

[0034] Polyethylene glycol 15~20%,

[0035] 1-Hydroxycyclohexyl phenyl ketone-photoinitiator 184 5~10%;

[0036] The particle size of the silica particl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of novel matte anti-static release paper. One surface of release paper body paper is coated with a coating layer through a coating machine, and one surface of a thin film layer is coated with a matte anti-static coating with a thickness of 0.2-2 micrometres. Under the influence of the used ultraviolet rays which are of a wave band of 280-350nm and of an illumination of 1200mW / cm<2>, components, contained in the matte anti-static coating, including 2-6% of silica particles, 20-30% of acrylic polyol with the average molecular weight of 500-2000, 35-45% of resin of polyoxyalkylene polyols with the average molecular weight of 200-2500, 15-20% of polyethylene glycol and 5-10% of 1-1-hydroxy-cyclohexyl phenyl ketone-photoinitiator 184 react to obtain the matte anti-static coating. The thickness of the matte anti-static coating is 4-10 micrometres. The preparation method of the novel matte anti-static release paper not only solves the problems that the binding force between the coating layer and the release agent coating of the release paper is not strong and the release force between the coating layer and the release agent coating of the release paper is not stable, but also promotes the anti-static performance of the surface of the film, and meanwhile promotes the anti-scraping performance.

Description

technical field [0001] The invention relates to a preparation method of a novel matte antistatic release paper, in particular to a preparation method of a novel matte antistatic release paper with high adhesion and stable peeling force. Background technique [0002] Release paper, also known as release paper and anti-adhesive paper, is mainly used to stick the adhesive layer on the surface of the tape to protect the surface of the tape. The existing release paper is generally coated with a film layer (the material used is mainly polyethylene) on the surface of the bottom paper layer of the release paper, and then coated with a layer of release agent coating on the surface of the film layer (The material used is mainly silicone oil) to obtain a release paper. However, due to the high flatness of the coating layer and the poor adhesion between the release agent coating and the coating layer, when the release paper is attached to the film coated with a high-viscosity adhesive,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/00D21H19/22D21H19/28
Inventor 金闯张庆杰
Owner JIANGSU SIDIKE NEW MATERIALS SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com