Silicone gel composition for manufacturing breast prosthesis, and preparation method thereof

A technology of silicone gel and composition, which is applied in the field of silicone gel composition and its preparation, can solve the problems of poor elasticity and softness of prosthetic breasts, increase the burden on the wearer of prosthetic breasts, and the hand feeling is not close enough to achieve anti-delamination Effects of ability improvement, longer usable time, and lower density

Active Publication Date: 2015-02-04
SUZHOU AIMER UNDERWEAR CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the prosthetic breasts made of existing silicone gels have poor elasticity and softness, the hand feeling is not close to the fat structure of the human body, and the proportion is relatively large, which increases the burden on the wearers of the prosthetic breasts. High, it is easy to delaminate after standing for a long time at room temperature during use, and the wearing comfort is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] A kind of silicone gel composition for making prosthetic milk is characterized in that, the composition of described silicone gel composition comprises by weight percentage:

[0050] Dimethicone Gel 68%;

[0051] Simethicone 31.5%;

[0052] Fumed silica 0.1%;

[0053] Prefoamed polymer microspheres 0.2%;

[0054] Branched vinyl silicone oil 0.1%;

[0055] Color paste 0.1%.

Embodiment 2

[0057] A kind of silicone gel composition for making prosthetic milk is characterized in that, the composition of described silicone gel composition comprises by weight percentage:

[0058] Dimethicone Gel 68%;

[0059] Simethicone 29.5%;

[0060] Fumed silica 0.5%;

[0061] Prefoamed polymer microspheres 1%;

[0062] Branched vinyl silicone oil 0.5%;

[0063] Color paste 0.5%.

Embodiment 3

[0065] A kind of silicone gel composition for making prosthetic milk is characterized in that, the composition of described silicone gel composition comprises by weight percentage:

[0066] Dimethicone Gel 70.5%;

[0067] Simethicone 28%;

[0068] Fumed silica 0.3%;

[0069] Prefoamed polymer microspheres 0.6%;

[0070] Branched vinyl silicone oil 0.3%;

[0071] Color paste 0.3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
viscosityaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The present invention provides a silicone gel composition for manufacturing breast prosthesis. The silicone gel composition is characterized by comprising, by weight, 68-73% of a dimethylsiloxane gel, 24.5-31.5% of dimethicone, 0.1-0.5% of fumed silica, 0.2-1% of pre-expanded polymer microspheres, 0.1-0.5% of branch chain type vinyl silicone oil, and 0.1-0.5% of a color paste. The present invention further provides a silicone gel composition preparation method. Compared to the silicone gel composition in the prior art, the silicone gel composition of the present invention has characteristics of low specific gravity, small hardness, layering resistance and low production cost, wherein the manufactured breast prosthesis can well simulate tactility of human adipose tissue. The preparation method has characteristics of simple preparation process and easy operation, high flexibility, and wide application range, wherein most of the operation steps are not specifically limited by operation time limit and environment.

Description

technical field [0001] The invention relates to a silicone gel composition and a preparation method thereof, in particular to a silicone gel composition for making lightweight silicone prosthetic milk and a preparation method thereof. Background technique [0002] Prosthetic breasts, also known as artificial breasts, false breasts. It is a substitute for breast cancer patients after resection (a type of prosthesis, which is different from adult products, and is a surgical rehabilitation product). The commonly used material for prosthetic breasts is medical silicone. The commonly used material for prosthetic milk is solid medical silicone rubber. Silicone rubber has good biocompatibility, is non-irritating, non-toxic, non-allergic to human tissues, and has very little rejection of the body; it has good physical and chemical properties and is compatible with body fluids and It can maintain its original elasticity and softness during tissue contact without being degraded, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/18A61L27/16A61L27/14A61L27/02A61L27/52A61L27/50
Inventor 翁良
Owner SUZHOU AIMER UNDERWEAR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap