A concrete and light-weight technology, applied in the field of concrete, can solve the problems of construction burden and heavy weight, and achieve the effect of reducing the burden
Inactive Publication Date: 2014-04-30
张家界万众新型建筑材料有限公司
View PDF7 Cites 4 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, the existing concrete imposes a strong burden on the construction due to its heavy weight
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0012] A light weight concrete, its raw material components by weight, 100 parts of cement, 50 parts of water, 65 parts of PC, 12.5 parts of quicklime, 6 parts of carbon powder, 2 parts of calcium carbonate, 0.1 part of zinc sulfate.
Embodiment 2
[0014] A lightweight concrete, the raw materials of which are, by weight, 100 parts of cement, 50 parts of water, 60 parts of PC, 15 parts of quicklime, 5 parts of carbon powder, 4 parts of calcium carbonate and 0.05 part of zinc sulfate.
Embodiment 3
[0016] A lightweight concrete, the raw materials of which are, by weight, 100 parts of cement, 50 parts of water, 70 parts of PC, 10 parts of quicklime, 7 parts of carbon powder, 1 part of calcium carbonate, and 0.2 parts of zinc sulfate.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses lightweight concrete. The lightweight concrete comprises the following components in parts by weight: 100 parts of cement, 50 parts of water, 60-70 parts of PC (polycarbonate), 10-15 parts of quick lime, 5-7 parts of carbon powder, 1-4 parts of calcium carbonate and 0.05-0.2 part of zinc sulfate. By breaking a conventional concrete formula, replacing a part of cement with the PC, activating through calcium carbonate and zinc sulfate and reinforcing through the quick lime, the obtained lightweight concrete has the engineering value of concrete and is lighter than conventional concrete by more than 10 times, so that great burden is reduced for engineering.
Description
technical field [0001] The present invention relates to a concrete. Background technique [0002] Concrete, referred to as "concrete (tóng)": refers to the collective name of engineering composite materials that use cementitious materials to cement aggregates into a whole. Generally speaking, the term concrete refers to cement as cementing material, sand and stone as aggregate; mixed with water (with or without admixtures and admixtures) in a certain proportion, and obtained by stirring, molding and curing. Cement concrete, also known as ordinary concrete, is widely used in civil engineering. However, the existing concrete imposes a strong burden on construction due to its heavy weight. Contents of the invention [0003] The technical problem to be solved by the invention is to overcome the existing defects and provide a lightweight concrete with a lighter texture. [0004] The purpose of the present invention is specifically achieved through the following technical sol...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C04B28/00
Inventor 唐萍
Owner 张家界万众新型建筑材料有限公司