Railroad rail track pad and cross-linked foam

A technology for cross-linking foam and track pads, which is applied in the field of cross-linking, can solve the problems of insufficient foaming and balance of physical properties, and achieve small compression set, excellent processability, high tensile strength and elongation. effect of length

Active Publication Date: 2014-11-05
MITSUI CHEM INC
View PDF12 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when such EPDM is used for a track pad, since the main chain does not contain a diene, although the weather resistance is good, the foamability and the balance of physical properties are insufficient.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Railroad rail track pad and cross-linked foam
  • Railroad rail track pad and cross-linked foam
  • Railroad rail track pad and cross-linked foam

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0199] [Preparation of rubber composition and its vulcanized rubber molding]

[0200] The rubber composition used in the present invention can be prepared by using an internal mixer such as a Banbury mixer, a kneader, or an intermix, in Additives such as ethylene·α-olefin·non-conjugated polyene copolymer rubber [I], carbon black, rubber reinforcing agent, inorganic filler, softener, etc. are kneaded at a temperature of 80 to 170°C for 2 to 20 minutes, and then, Use rolls such as open rolls or a kneader to knead sulfur, add vulcanization accelerators, vulcanization aids, foaming agents, and foaming aids as needed, and knead at a roll temperature of 40-80°C for 5- 30 minutes and then tableted, thus prepared.

[0201]

[0202] The cross-linked rubber used in the present invention is characterized by cross-linking the rubber composition described above. As a method of crosslinking the rubber composition, the following two methods are mentioned, for example. As the first metho...

Embodiment 1 and 2

[0226] Use the following copolymers 1 and 2 to prepare the compositions shown in Table 1, use a mold of 125mm x 140mm x 10mmt, fill the mold with the composition of Table 1 at a volume filling rate of 100%, and heat it at 130°C for 15 minutes Carry out cross-linking and foaming once under the same conditions, and then use a mold of 200mm×200mm×1mmt to fill the cross-linked foam obtained from the first cross-linking and foaming, and perform two times of cross-linking under the condition of 170°C×10 minutes The foamed cross-linked rubber for railway track pads was produced by foaming, and various physical properties were evaluated.

[0227] [Copolymer 1]

[0228] Ethylene·α-olefin·non-conjugated polyene random copolymer produced by the same method as in Example 1 of International Publication No. WO2010 / 064574 (the molar ratio is different and the feed amount is adjusted)

[0229] [C-1] = ENB

[0230] [C-2] = VNB

[0231] Requirement (1): [B]=36.8 mol%

[0232] Requirement (2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
compression setaaaaaaaaaa
Login to View More

Abstract

Provided is a railroad rail track pad obtained by crosslinking a composition containing an ethylene / alpha-olefin / non-conjugated polyene random copolymer which includes structural units of ethylene [A], C3-20alpha-olefin [B], and a non-conjugated polyene [C-1] containing one of the structures of formulae (I) and (II) [formula (I) is partial structure of a cyclic olefin], and a non-conjugated polyene [C-2] containing two or more of structures of formulae (I) and (II), and which fulfills (1) [B] is a 10-50 mol%, (2) the total of [C-1] and [C-2] is 1.0-6.0 mol%, (3) [C-1] / [C-2] is 75 / 25 to 99.5 / 0.5, (4) ML1+4(100°C) is 10-90, (5) the iodine value of [C-2] is 0.1-3.0g / 100g, and (6) 50 > flow activation energy (Ea) > 35.

Description

technical field [0001] The present invention relates to a track pad for railway rails and a cross-linked foam formed of a cross-linked body or a cross-linked foam. More specifically, it relates to a rail mat for railway rails and a crosslinked foam obtained from a rubber composition exhibiting sufficient high foamability, and more specifically, it relates to a railroad track mat formed of a crosslinked body or a crosslinked foam. A track pad for a railroad track and a cross-linked foam. The cross-linked body or cross-linked foam requires various physical properties (including weather resistance) such as a moderate elastic modulus, high tensile strength and elongation, and small compression set. ), and form a low specific gravity rubber molded body that is also excellent in processability. Background technique [0002] Railroad mats are used as anti-vibration materials for reducing vibration and noise generated when vehicles run on railroad tracks (railways). The railway ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityApplications(China)
IPC IPC(8): E01B9/68C08F210/18C08L23/08
CPCC08J2201/026E01B9/681C08J2323/08C08L2312/00C08L23/08C08J9/103C08L23/16C08L2314/06C08J9/0014C08J9/0066C08F210/18E01B9/68C08F210/06C08F236/20C08F2500/17C08F2500/20C08F2500/25
Inventor野口裕司竹原明宣野中修一
OwnerMITSUI CHEM INC