Method for preparing polyurethane modified silicone two-component room temperature curing elastomer adhesive

A polyurethane modification, room temperature curing technology, applied in the direction of polyurea/polyurethane adhesives, adhesives, adhesive types, etc., can solve the problems of poor high temperature resistance of polyurethane and poor adhesion of silicone materials, and achieve good The effect of high and low temperature resistance, material cost reduction, and short production cycle

Active Publication Date: 2017-05-03
道一高分子聚合物(宁波)有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the shortcomings of poor high temperature resistance of polyurethane and poor bonding of silicone materials, the purpose of this invention is to provide a method for preparing polyurethane modified silicone two-component room temperature curing elastomer adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention will be further described in detail below in conjunction with specific embodiments.

[0026] The method for preparing the two-component room temperature curing elastomer adhesive of the present invention comprises the following steps:

[0027] (1) Preparation of raw materials: The mixture of hydroxypropyl-terminated silicone oil (relative average molecular weight Mw=1000) and glycerol was subjected to vacuum dehydration treatment at 100 ° C ~ 110 ° C for 3 ~ 4 hours before the reaction started, and the mixture containing Hydroxyl-terminated (-OH) components with a water content of less than 0.05%. The mixing mass ratio of the two is 20~22:1.

[0028] (2) Preparation of component A: the aromatic polyisocyanate, hydroxyl-terminated (-OH) components (hydroxypropyl-terminated silicone oil and glycerol) are prepared according to functional groups n(NCO / OH)=1.8~1.82, catalyst dilauric acid The amount of dibutyltin added is 0.05%~0.06% of the total mass...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
breaking strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a polyurethane-modified organosilicon double-component room-curing elastomer adhesive, which comprises the following steps: (1) uniformly mixing hydroxypropyl-terminated silicone oil and glycerol, and dehydrating to obtain a hydroxyl-terminated (-OH) component; (2) reacting aromatic polyisocyanate, the hydroxyl-terminated (-OH) component and dibutyltin dilaurate to obtain a component A; (3) adding vapor-phase silica white, carbon black and talcum powder into the container filled with hydroxy silicone oil and dihydroxy polysiloxane, adding a catalyst, adding 3-aminopropyl triethoxy silane, finally adding a defoaming agent, uniformly mixing, and drying to obtain a component B; and (4) uniformly mixing the component A and component B in a mass ratio of 12:(23.5-24), and curing at room temperature for 4-5 hours. The elastomer adhesive prepared by the method has the advantages of favorable tear resistance, excellent high / low temperature resistance and excellent binding property. The preparation method is easy to operate and accessible in raw materials, and lowers the preparation cost.

Description

technical field [0001] The invention relates to a method for preparing a polyurethane modified organosilicon two-component room temperature curing elastomer adhesive with high temperature resistance, low temperature resistance, good elasticity and excellent performance, belonging to the technical field of new chemical materials. Background technique [0002] Polyurethane (PU) is short for polyurethane. All compounds containing many repeating carbamate (-NH-COO-) or urea (-NH-CO-NH) groups on the polymer backbone are collectively referred to as polyurethane. [0003] Polyurethane is a block polymer consisting of soft and hard segments. The soft segment of the polyurethane macromolecule is generally composed of flexible segments such as long-chain polyols or polyethers, which are randomly coiled. The polyurethane hard segment (rigid segment) is a rigid chain consisting of aryl, urethane and substituted urea groups obtained from diisocyanates, diols, diamines and other chain ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J175/04C09J11/04C09J11/06C08G18/65C08G18/61C08G18/32C08G18/12C08G18/24C08G18/18
Inventor 罗宏李新跃勾雪功刘凯
Owner 道一高分子聚合物(宁波)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap